本发明专利技术涉及一种钢材，具体地说，涉及一种具有高耐磨性能的滚刀刀圈专用钢材，本发明专利技术提出一种适合极端复杂的地质情况的具有高耐磨性能的滚刀 刀圈专用钢材，所述钢材由下述质量百分比的组分组成：0.5%‑0.8%的C，3.5%‑5.5%的Cr，1.5%‑3%的Mo，2%‑3%的W，0.5%‑2%的V，余量为铁，本发明专利技术的专用钢材添加了适量的Cr、Mo、W、V，使本技术方案的钢材具有了使滚刀刀圈可以适应极端复杂地质情况的耐磨性能、耐高温性能，提高了滚刀刀圈的适应性，可以适应更加复杂的地质情况。

Special steel for hob ring with high wear resistance

The invention relates to a steel, in particular, relates to a high wear resistance of the cutter ring of special steel, the invention provides a suitable geological conditions are extremely complicated hob cutter ring special steel with high abrasion resistance, the quality of steel is composed of the following components: 0.5% percentage 0.8% the 3.5% C, 5.5% Cr, 1.5% Mo 2% 3%, 3% W, 0.5% V 2%, allowance for iron, special steel of the invention to add the right amount of Cr, Mo, W, V, the technical scheme of the steel has the cutter ring can adapt to extreme complex wear performance and quality of the high temperature performance, improve the adaptability of the cutter ring, can adapt to more complex geological conditions.

【技术实现步骤摘要】
具有高耐磨性能的滚刀刀圈专用钢材
本专利技术涉及一种钢材，具体地说，涉及一种具有高耐磨性能的滚刀刀圈专用钢材。
技术介绍
目前市场上滚刀刀圈的专用材质主要有两种：H13与G1材质的钢材，其中H13属于热作模具钢，H13具有良好的韧性，能够适用于多数的地层的破岩工作，但在岩石强度较高的情况下，表现出耐磨性能不足的问题，G1材质的钢材具有很好的耐磨性能，但存在韧性不足的问题，虽然采用上述两种材质生产制造的滚刀刀圈能够适用于绝大部分地层的掘进，但在极端复杂的地质情况下，需要滚刀刀圈具有高的耐磨性能与韧性，但是现有技术中的钢材都很难达到要求。
技术实现思路
为了解决上述问题，本专利技术提出一种适合极端复杂的地质情况的具有高耐磨性能的滚刀刀圈专用钢材，其具体的技术方案如下：一种具有高耐磨性能的滚刀刀圈专用钢材，所述钢材由下述质量百分比的组分组成：0.5%-0.8%的C，3.5%-5.5%的Cr，1.5%-3%的Mo，2%-3%的W，0.5%-2%的V，余量为铁。优选地，其中的含量限定为方程式：5.5%≤Cr和Mo质量百分比≤8%，5.5%≤Cr和W的质量百分比≤8%。优选地，其中的含量限定为方程式本文档来自技高网...

【技术保护点】
一种具有高耐磨性能的滚刀刀圈专用钢材，其特征在于：所述钢材由下述质量百分比的组分组成：0.5%‑0.8%的C，3.5%‑5.5%的Cr，1.5%‑3%的Mo，2%‑3%的W，0.5%‑2%的V，余量为铁。

【技术特征摘要】
1.一种具有高耐磨性能的滚刀刀圈专用钢材，其特征在于：所述钢材由下述质量百分比的组分组成：0.5%-0.8%的C，3.5%-5.5%的Cr，1.5%-3%的Mo，2%-3%的W，0.5%-2%的V，余量为铁。2.根据权利要求1所述的具有高耐磨性能的滚刀刀圈专用钢材，其特征在于：含量限定为方程式：5.5%≤Cr和Mo质量百分比≤8%，5.5...

【专利技术属性】
技术研发人员：刘玉海，王大可，张学强，王宏光，闫国成，
申请(专利权)人：山东天工岩土工程设备有限公司，
类型：发明
国别省市：山东,37