The invention relates to a zinc alloy abrasive formula and processing technology, which belongs to the field of abrasive and processing technology. The percentage of its mass is: aluminum: 0.40 ~ 2%, magnesium: 0.00001 - 0.003%, zinc: 97 - 98%. A process Aluminum Alloy abrasive, which comprises the following steps: the raw materials according to the elemental ratios were prepared by melting, zinc alloy wire, wire drawing, annealing; the zinc alloy wire, cut the preparation of abrasives, the diameter and length of the zinc alloy wire cut off ratio of 1: 1; spheroidizing treatment of after cutting the zinc alloy for different time; aging treatment. Owing to the adoption of the above technical scheme, the advantages and positive effects of the invention are: it can be used for surface whitening treatment of various alloy castings, and can also be used as additive for metal smelting.
【技术实现步骤摘要】
一种锌合金磨料配方及其加工工艺
本专利技术涉及一种锌合金磨料配方及其加工工艺，属于磨料及加工
技术介绍
目前，通过利用喷(抛)丸(砂)对金属表面进行处理。而其中的砂材磨料是决定处理效果的关键因素。
技术实现思路
本专利技术所要解决的技术问题是：提供一种锌合金磨料配方及其加工工艺，其磨料可用于各种合金铸件的表面增白处理，也可用于金属冶炼的添加料。本专利技术解决其技术问题所采用的技术方案是：一种铝合金磨料配方，其特征是：按质量的百分比为：铝：0.40～2.00％，镁：0.00001～0.003％，锌：97～98％。一种铝合金磨料的加工工艺，其特征是：包括以下步骤：(1).将上述原料单质按照比例制备锌合金丝，通过熔炼、拉丝、退火；熔炼：将上述原料按上述比例，按一定顺序投放到熔炼设备中，通过高温将其变成液态，让其充分混合后，放置到特制的磨具中去后冷却，使其变成直径4mm-6mm的杆状盘条；拉丝：按最终成品的要求，选用不同直径的磨具，从0.4mm-2.0mm，进行挤压拉丝；退火：将拉出的半成品丝状产品，放到保温容器中保持温度100℃-150℃之间，4-8小时，冷却后重...
【技术保护点】
一种锌合金磨料配方，其特征是：按质量的百分比为：铝：0.40～2.00％，镁：0.00001～0.003％，锌：97～98％。
【技术特征摘要】
1.一种锌合金磨料配方，其特征是：按质量的百分比为：铝：0.40～2.00％，镁：0.00001～0.003％，锌：97～98％。2.一种锌合金磨料的加工工艺，其特征是：包括以下步骤：(1).将上述原料单质按照比例制备锌合金丝，通过熔炼、拉丝、退火；熔炼：将上述原料按上述比例，按一定顺序投放到熔炼设备中，通过高温将其变成液态，让其充分混合后，放置到特制的磨具中去后冷却，使其变成直径4mm-6mm的杆状盘条；拉丝：按最终成品的要求，选用不同直径的磨具，从0.4mm-2.0mm，进行挤压拉丝；退火：将拉出的半成品丝状产品，放到保温容器中保持温度100℃-150℃之间，4-8小时，冷却后重复上述拉丝操作，直到达到要求的锌合金丝...
【专利技术属性】
技术研发人员：邱锋，孙清，
申请(专利权)人：盐城赛普金属制品有限公司，
类型：发明
国别省市：江苏,32