Radiation building coating and the preparation method of the invention discloses an indoor control, comprising the following components by weight: 10 20 yttrium nitrate, lanthanum nitrate 1 3, four two 1 2 adenosine phosphate, purine 5 8, 7 12 film-forming agent, water 30 90, thickening agent 3 5 copies, 5 copies of the 2 radiation protection agent. The present invention obtained through the above formula for coating has the characteristics of anti radiation, the coating on indoor wall in building material, nuclear radiation can prevent and eliminate radiation have been exposed to radiation pollution, not only applicable to the use of living room interior radiation, can also be used in the laboratory for nuclear radiation solution can eliminate misoperation due to long radiation problems, solve the existing paint with radiation problems, provides a low cost, simple preparation of the indoor radiation protection of architectural coatings.
【技术实现步骤摘要】
一种室内防辐射建筑涂料及其制备方法
本专利技术涉及涂料领域，尤其涉及一种室内防辐射建筑涂料及其制备方法。
技术介绍
目前，建筑用内墙一般都采用涂料涂装，涂料涂饰于物体表面能与基体材料很好粘结并形成完整而坚韧的保护膜，建筑涂料具有装饰功能、保护功能和居住性改进功能。各种功能所占的比重因使用目的不同而不尽相同。装饰功能是通过建筑物的美化来提高它的外观价值的功能。具有核辐射的单位的建筑一般都采用严格的防护措施，墙壁加厚，穿铅衣进行操作，非常麻烦，随着科技的发展，核辐射物质逐渐被应用于普通
，如转基因实验室的基因杂交，采用温和的磷素核辐射物质，该类物质为液体容易，一旦溅落于建筑的表面，不容易擦拭，辐射会长久存在，给实验者的身体造成不可逆转的损害，现有的处理方法要保证完全去除核辐射残留，只能采用等待的方式，等核辐射自然衰减至无害的剂量，往往会耽误实验的进度。因此，现有技术还有待于改进和发展。
技术实现思路
鉴于上述现有技术的不足，本专利技术的目的在于提供一种室内防辐射建筑涂料及其制备方法，旨在解决室内建筑表面的核辐射物质附着及去除问题。本专利技术的技术方案如下：一种室内防...
【技术保护点】
一种室内防辐射建筑涂料，其特征在于，按重量份数计由以下组分组成：硝酸钇10‑20份；硝酸镧1‑3份；四磷酸二腺苷1‑2份；嘌呤5‑8份；成膜剂7‑12份；水30‑90份；增稠剂3‑5份；防辐射剂2‑5份。
【技术特征摘要】
1.一种室内防辐射建筑涂料，其特征在于，按重量份数计由以下组分组成：硝酸钇10-20份；硝酸镧1-3份；四磷酸二腺苷1-2份；嘌呤5-8份；成膜剂7-12份；水30-90份；增稠剂3-5份；防辐射剂2-5份。2.根据权利要求1所述的室内防辐射建筑涂料，其特征在于，所述嘌呤由黄嘌呤，鸟嘌呤，腺嘌呤，乙酰腺嘌呤，乙酰次黄嘌呤，6-氯嘌呤，6-巯基嘌呤，6-氨基-2-甲氧基嘌呤中一种或几种组成。3.根据权利要求1所述的室内防辐射建筑涂料，其特征在于，所述成膜剂由三聚氰酸环氧，丙二醇苯醚，丁醚醋酸酯，磷酸二氢盐，沥青乳剂，刺槐豆胶，半乳甘露糖中的一种或几种组成。4.根据权利要求1所述的室内防辐射建筑涂料...
【专利技术属性】
技术研发人员：陈强，
申请(专利权)人：佛山市三水区嫚娅环保科技有限公司，
类型：发明
国别省市：广东,44