The invention provides a degradable medical spatula, spatula composition and ratio of starch is 80 fiber 10 90 copies, 20 copies, 10 copies of the 5 plasticizer, the fiber is polyvinyl alcohol (PVA) fiber, its preparation method comprises the following steps: 1. according to the proportion of raw material preparation and through the high-speed dispersion machine rapid mixing uniformity; 2. mixture into the double screw extruder extrusion, the temperature control between 95 to 120 DEG C, the speed is 100 ~ 150r/min, masterbatch extrusion after cooling; 3. will be added to the masterbatch injection molding machine, injection molding, prepared spatula; 4. vacuum drying spatula, and after disinfection, vacuum packaging. The invention uses starch as the raw material to reduce the pressure and depress the tongue plate, reduces the environmental pollution, and has rich source of raw materials, so as to achieve the purpose of saving energy and environmental protection.
【技术实现步骤摘要】
一种可降解医用压舌板及制备方法
本专利技术涉及医疗器械领域,具体涉及一种可降解医用压舌板及制备方法。
技术介绍
压舌板是医生在咽部视诊中,用来下压舌头以方便检查周围器官及组织的工具。目前临床上使用的压舌板主要分为两种,一种是木质、竹质、塑料制成的一次性压舌板,另一种是不锈钢等金属材料制成的循环用压舌板。循环用压舌板经消毒后可往复循环使用,但难以保证每次消毒彻底,卫生性较差,存在交叉感染的风险;一次性压舌板方便卫生,没有感染风险,但是木质、竹制的压舌板会造成一定的材料浪费,尤其是现在材料资源越来越少的情况下,塑料制成的一次性压舌板在使用之后的会对环境造成污染,不利于环境的持续发展。
技术实现思路
为了解决上述技术问题本专利技术提供一种可降解医用压舌板及制备方法,一次性使用,降低感染风险,使用之后可降解减少了环境污染。本专利技术的技术方案是:一种可降解医用压舌板,压舌板组成成分及配比是:淀粉80-90份,纤维10-20份,增塑剂5-10份。所述纤维是聚乙烯醇(PVA)纤维。一种可降解医用压舌板的制备方法,其步骤是:1.按照配比准备原料,通过高速分散机迅速混合分散均匀;2.将混合料加入双螺杆挤出机塑化挤出,各区温度控制在95~120℃之间,转速为100~150r/min,挤出后冷却造母粒;3.将上述母粒加入到注塑机内,进行注塑成型,制得压舌板;4.真空干燥压舌板,并且进行消毒处理之后,进行真空包装。本专利技术的有益效果是:本专利技术以淀粉为原料制得可降解压舌板,减少环境污染,且原料来源丰富,更好地实现节能、环保目的。具体实施方式下面对本专利技术做清楚完整的描述,以使 ...
【技术保护点】
一种可降解医用压舌板,其特征在于,所述压舌板组成成分及配比是:淀粉80‑90份,纤维10‑20份,增塑剂5‑10份。
【技术特征摘要】
1.一种可降解医用压舌板,其特征在于,所述压舌板组成成分及配比是:淀粉80-90份,纤维10-20份,增塑剂5-10份。2.根据权利要求1所述的一种可降解医用压舌板,其特征在于,所述纤维是聚乙烯醇(PVA)纤维。3.一种权利要求2所述的一种可降解医用压舌板的制备方法,其特征在于,其步骤是...