The invention discloses a preparation method of Acrylic Rosin Based aromatic polyurethane. The ester, 250~320 quality Acrylic Rosin GMA 100 phr toluene diisocyanate and 1.8~2.1 2, 4 quality two butyl two dilaurates dissolved in toluene 666~815 into a reaction kettle, a stirring speed of 300 r/min, under the protection of N2 is heated to 30 to 60 DEG C, every 30 minutes acetone two n-butylamine method for the determination of the content of NCO, NCO to be content to the theoretical value when adding 8~18 mass of a chain extender 1, 4 butanediol, to NCO content is zero end reaction of Acrylic Rosin Based aromatic polyurethane resin. The polyol prepared by RAG has good storage stability at room temperature, and the coating has the characteristics of high gloss, flexibility and adhesion, high hardness and high impact strength.
【技术实现步骤摘要】
丙烯酸松香基芳香族型聚氨酯的制备方法
本专利技术涉及丙烯酸松香基芳香族型聚氨酯树脂的制备方法。
技术介绍
聚氨酯是指分子链中含有大量氨基甲酸酯键（-NHCOO-）重复结构单元的一类聚合物，是一种有机高分子材料，具有耐磨、耐腐蚀、耐高温等优良性能，产品具有配方灵活、分子设计性强等特点，广泛应用于泡沫塑料、纤维、弹性体、合成革、涂料、胶黏剂等领域。聚氨酯由聚醚或聚酯多元醇、多异氰酸酯以及小分子扩链剂反应生成。制备方法有（1）预聚体法：由异氰酸酯与多元醇在一定条件下反应生成预聚体，然后向预聚体中加入扩链剂进行链增长生成高分子化合物，可根据反应要求，加入适量的溶剂和催化剂调节体系中的粘度和反应速率。（2）一步法：将聚酯或聚醚多元醇、多异氰酸酯以及其它助剂如催化剂、扩链剂等一次性加入，在快速搅拌下混合均匀，使聚合、扩链以及固化等反应在短时间内几乎同时进行，即可得到聚氨酯高分子材料。随着科学技术的发展和生活水平的提高，人们对材料性能的要求越来越高，聚氨酯产品种类、使用范围、产业规模快速扩展，已发展成为最快的高分子合成材料工业之一。松香作为一种丰富的天然可再生林产资源，在日常生...
【技术保护点】
一种丙烯酸松香基芳香族型聚氨酯树脂的制备方法，其特征在于具体步骤为：将250~320质量份丙烯酸松香GMA的酯化物、100.0质量份甲苯‑2，4‑二异氰酸酯和1.8~2.1质量份二丁基二月桂酸锡溶解于666~815质量份甲苯，将其加入至反应釜中，设置搅拌速度为300 r/min，N2保护下加热至30～60℃进行反应，每隔30分钟用丙酮‑二正丁胺法测定‑NCO含量，待‑NCO含量降至理论值时，加入8~18质量份的扩链剂1，4‑丁二醇，继续反应至‑NCO含量为零时结束反应，得到丙烯酸松香基芳香族型聚氨酯树脂；所述化学试剂：丙烯酸松香GMA酯化物，自制，酸值为4.0 mg KOH·g
【技术特征摘要】
1.一种丙烯酸松香基芳香族型聚氨酯树脂的制备方法，其特征在于具体步骤为：将250~320质量份丙烯酸松香GMA的酯化物、100.0质量份甲苯-2，4-二异氰酸酯和1.8~2.1质量份二丁基二月桂酸锡溶解于666~815质量份甲苯，将其加入至反应釜中，设置搅拌速度为300r/min，N2保护下加热至30～60℃进行反应，每隔30分钟用丙酮-二正丁胺法测定-NC...
【专利技术属性】
技术研发人员：余彩莉，边峰，张发爱，陈勇，
申请(专利权)人：桂林理工大学，
类型：发明
国别省市：广西,45