The invention discloses a bamboo preparation process comprises the following steps: A. bamboo water cleaning; B. bamboo placed by hydrochloric acid, sodium chloride and water according to the mass ratio of the immersion ratio of 1:1:19 mix in the prepared, heated to 30 DEG C for three days; C. B will be a good soaking step the bamboo tube removed and placed in freezer refrigeration for 1 hours; D. C steps after freezing out and placed in bamboo sulfur, zinc stearate and water according to the mass ratio of the immersion ratio of 3:7:21 mix in the prepared, heated to 75 DEG C for 6 hours; E. D will step out a good soaking bamboo. With salt water rinse and drying; F. E will do the bamboo cutting, drying steps after setting bamboo treated by the invention has good flexibility, very suitable for making all kinds of Arts and crafts.
【技术实现步骤摘要】
一种竹片的制备工艺
本专利技术涉及一种竹片的制备工艺。
技术介绍
竹片是竹筒经开片后形成的窄长片材,其主要用来编制各种工艺品。而在编制工艺品时,通常会由于竹片太硬、没有柔韧性而容易发生折断或是伤手的,不仅造成了竹片废品的产生还对编制人员的人身安全造成了隐患。为此,人们在制备竹片的过程中,会对竹片竹片进行相应的处理,从而使其符合编制要求。
技术实现思路
本专利技术的目的是克服现有产品中的不足,提供一种竹片的制备工艺。为了达到上述目的,本专利技术是通过以下技术方案实现的:一种竹片的制备工艺,包括以下步骤:A.将竹筒用水清洗;B.将竹筒放入由盐酸、氯化钠、水按照质量比为1:1:19的比例混合制得的浸泡液中,加热至30℃浸泡三天;C.将B步骤浸泡好的竹筒取出并放入冷藏室冷藏1个小时;D.将C步骤冷冻后的竹筒取出并放入由硫磺、硬脂酸锌以及水按照质量比为3:7:21的比例混合制得的浸泡液中,加热至75℃浸泡6小时;E.将D步骤浸泡好的竹筒取出,用盐水漂洗干净、并烘干;F.将E步骤晾干好的竹筒开片、定型。本专利技术的有益效果如下:经过本专利技术处理后的竹片具有很好的柔软性,非常适于编制各种工艺品。具体实施方式下面对本专利技术的技术方案作进一步说明:实施例1:一种竹片的制备工艺,包括以下步骤:A.将竹筒用水清洗;B.将竹筒放入由盐酸、氯化钠、水按照质量比为1:1:19的比例混合制得的浸泡液中,加热至30℃浸泡三天;C.将B步骤浸泡好的竹筒取出并放入冷藏室冷藏1个小时;D.将C步骤冷冻后的竹筒取出并放入由硫磺、硬脂酸锌以及水按照质量比为3:7:21的比例混合制得的浸泡液中,加热 ...
【技术保护点】
一种竹片的制备工艺,其特征在于,包括以下步骤:A.将竹筒用水清洗;B.将竹筒放入由盐酸、氯化钠、水按照质量比为1:1:19的比例混合制得的浸泡液中,加热至30℃浸泡三天;C.将B步骤浸泡好的竹筒取出并放入冷藏室冷藏1个小时;D.将C步骤冷冻后的竹筒取出并放入由硫磺、硬脂酸锌以及水按照质量比为3:7:21的比例混合制得的浸泡液中,加热至75℃浸泡6小时;E.将D步骤浸泡好的竹筒取出,用盐水漂洗干净、并烘干;F.将E步骤晾干好的竹筒开片、定型。
【技术特征摘要】
1.一种竹片的制备工艺,其特征在于,包括以下步骤:A.将竹筒用水清洗;B.将竹筒放入由盐酸、氯化钠、水按照质量比为1:1:19的比例混合制得的浸泡液中,加热至30℃浸泡三天;C.将B步骤浸泡好的竹筒取出并放入冷藏室冷藏1个小...