本发明专利技术涉及一种吸湿透气的羊毛复合面料，包括羊毛纤维和维纶纤维，所述羊毛纤维的规格为细度85s～150s、长度95～115mm；所述维纶纤维的规格为3.5～4.5dtex×50 ～ 75mm；其特征在于，还包括苎麻纤维和芳纶纤维。本发明专利技术所具有的优点是：在羊毛复合面料内增加苎麻纤维和芳纶纤维，苎麻纤维起到吸湿的作用，芳纶纤维有一定的硬度，能够支撑起一部分空洞，提高面料的透气性能。

A kind of moisture absorbing and breathable wool composite fabric

The invention relates to a composite wool fabric moisture permeability, including wool fiber and vinylon fiber, the wool fiber specifications for fineness of 85s ~ 150s and 95 ~ 115mm in length; the vinylon fiber size 3.5 ~ 4.5dtex * 50 ~ 75mm; characterized include ramie fiber and aramid fiber fiber. The advantages of the invention are: ramie fiber and aramid fiber are added into the wool compound fabric, ramie fiber plays the role of moisture absorption, and aramid fiber has certain hardness, which can support part of the cavity and improve the breathability of the fabric.

【技术实现步骤摘要】
一种吸湿透气的羊毛复合面料
本专利技术涉及纺织领域，特别涉及一种吸湿透气的羊毛复合面料。
技术介绍
现有技术中有一种羊毛面料，包括羊毛纤维和维纶纤维，所述羊毛纤维的规格为细度85s～150s、长度95～115mm；所述维纶纤维的规格为3.5～4.5dtex×50～75mm。这种羊毛面料具有保暖、富于弹性的特点。但是采用这种羊毛面料制成的衣物，吸湿透气性差，穿着闷热。
技术实现思路
针对上述缺点，本专利技术目的在于提供一种吸湿透气的羊毛复合面料，提高现有羊毛面料的吸湿透气性能。为实现上述目的，本专利技术采用的技术方案是：一种吸湿透气的羊毛复合面料，包括羊毛纤维和维纶纤维，所述羊毛纤维的规格为细度85s～150s、长度95～115mm；所述维纶纤维的规格为3.5～4.5dtex×50～75mm；其特征在于，还包括苎麻纤维和芳纶纤维；所述苎麻纤维的规格为细度25s～55s、长度30～65mm；所述芳纶纤维的规格为2.5～3.5dtex×45～80mm；所述苎麻纤维、芳纶纤维、羊毛纤维和维纶纤维的重量百分比为：20～35:18～40:55～75:40～60。本专利技术与现有技术相比所具有的优点是本文档来自技高网...

【技术保护点】
一种吸湿透气的羊毛复合面料，包括羊毛纤维和维纶纤维，所述羊毛纤维的规格为细度85s～150s、长度95～115mm；所述维纶纤维的规格为3.5～4.5dtex×50 ～ 75mm ；其特征在于，还包括苎麻纤维和芳纶纤维；所述苎麻纤维的规格为细度25s～55s、长度30～65mm；所述芳纶纤维的规格为2.5～3.5dtex×45 ～ 80mm；所述苎麻纤维、芳纶纤维、羊毛纤维和维纶纤维的重量百分比为： 20～35:18～40:55～75:40～60。

【技术特征摘要】
1.一种吸湿透气的羊毛复合面料，包括羊毛纤维和维纶纤维，所述羊毛纤维的规格为细度85s～150s、长度95～115mm；所述维纶纤维的规格为3.5～4.5dtex×50～75mm；其特征在于，还包括苎麻纤维和芳纶纤维；所述...

【专利技术属性】
技术研发人员：王妮，任晓，赵惠红，李红，
申请(专利权)人：江苏阳光集团有限公司，
类型：发明
国别省市：江苏,32