The invention provides a damping coating preparation method, which belongs to the coating technology field. The coatings prepared are mainly used for vibration reduction and noise reduction in automobiles, trains, ships, aircraft, construction machinery and other fields. The method is as follows: the acrylic emulsion, deionized water, stirring in the container, adding filler, mica powder, dispersing agent, defoaming agent, halogen-free flame retardant, in 500 ~ 600r/min speed, stirring after 20 ~ 28min to obtain a mixed solution; step 1) the mixture is added in the film agent, dispersing agent, defoaming agent, halogen-free flame retardant, in 100 ~ 120r/min speed, mixing 10 ~ 18min after adding thickening agent to adjust the consistency can be. The paint made by the invention has good damping, sound insulation, heat preservation and flame retardancy.
【技术实现步骤摘要】
阻尼涂料的制备方法
本专利技术涉及一种阻尼涂料，尤其涉及一种阻尼涂料的制备方法。
技术介绍
水性阻尼涂料具有良好的阻燃性、高附着力、耐腐蚀性、抗老化性、高阻尼性能且施工方便等优点，目前正被广泛应用在汽车、火车、轮船、飞机、工程机械和其他家用电器领域，起到隔声、吸声、减振和保温作用。阻尼涂料能够起到阻尼减振效果，主要取决于涂层中高分子链段之间、高分子与填料之间以及填料之间的相互作用，它们之间作用的强弱直接影响涂料的阻尼效能。现有技术中的水性阻尼涂料固含量较低，涂膜干燥后容易变形，阻尼温域较窄，阻尼值比较小，影响了水性阻尼涂料的实际使用。因此，能够拓宽高聚物的阻尼温度，提高水性阻尼涂料的固含量，使其在干燥过程中性质稳定、不易变形，同时有效提高阻尼性能和弹性模量，逐渐成为国内外学者开展研究的新课题。如公开号为CN103881491A，名称为“一种高阻尼性能的水性阻尼涂料的制备方法”的专利技术专利，该专利公开了的高阻尼性能的水性阻尼涂料的制备方法，包括以下步骤：(1)水性乳液的配制，(2)填料、助剂的加入，(3)成膜及调漆：再将上述溶液中加入8-20份双酯成膜助剂，以及2...
【技术保护点】
阻尼涂料的制备方法，其特征在于：包括以下步骤：1）称取丙烯酸乳液30～35份、去离子水20～30份，置于搅拌容器中，再加入填料20～40份、云母粉35～45份、分散剂1～3份、消泡剂0.2～0.8份、无卤阻燃剂0.2～0.8份，于500～600r/min的转速下，搅拌20～28min后得到混合液；2）向步骤1）得到的混合液中加入成膜助剂2～10份、分散剂0.5～1.5份、消泡剂0.1～0.4份、无卤阻燃剂0.1～0.4份，在100～120r/min的转速下，搅拌10～18min后加入增稠剂调节稠度后即可。
【技术特征摘要】
1.阻尼涂料的制备方法，其特征在于：包括以下步骤：1）称取丙烯酸乳液30～35份、去离子水20～30份，置于搅拌容器中，再加入填料20～40份、云母粉35～45份、分散剂1～3份、消泡剂0.2～0.8份、无卤阻燃剂0.2～0.8份，于500～600r/min的转速下，搅拌20～28min后得到混合液；2）向步骤1）得到的混合液中加入成膜助剂2～10份、分散剂0.5～1.5份、消泡剂0.1～0.4份、无卤阻燃剂0.1～0.4份，在100～120r/m...
【专利技术属性】
技术研发人员：王红丽，
申请(专利权)人：成都天航智虹知识产权运营管理有限公司，
类型：发明
国别省市：四川,51
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。