The invention discloses a spherical activated carbon ball making process, which comprises the following steps: (1) all the coal crushed to less than 100 mesh, moisture control in 12%~15%, (2) the pulverized coal and water, binder, mixing evenly, into the disc pelletizer, whose speed is 5~25r/min, disc angle 45 degrees 55 degrees; (3) preparing a screw feeder hopper, a scraper and a spray ball making machine side and bottom, can be adjusted to make the size of the ball. The beneficial effect of the invention is that it has high firmness, uniform texture, rapid molding, and can be used for waste.
【技术实现步骤摘要】
一种球形煤质活性炭制球工艺
本专利技术涉及活性炭制备
,具体为一种球形煤质活性炭制球工艺。
技术介绍
球形煤质活性炭采用优质褐煤或无烟煤及粘合剂、催化剂等经粉碎、混和、成球、干燥、碳化、活化而制成。球形煤质活性炭用于污水处理,效果较好;除此之外球形活性炭还可以用木质制作,其比重更轻,使用效果更加理想的。本工艺与其它煤质颗粒炭不同的是造球成型工艺,需要制得致密的有一定强度的炭球,活化工序基本相同。
技术实现思路
本专利技术的目的在于提供一种球形煤质活性炭制球工艺,以解决上述
技术介绍
中提出的问题。为实现上述目的,本专利技术提供如下技术方案:一种球形煤质活性炭制球工艺,包括如下步骤:(1)将煤全部破碎至<100网目,,水分控制在12%~15%,(2)将煤粉与水分、粘结剂拌均匀后,给入圆盘制球机,其转数为5~25r/min,盘倾角45°-55°;(3)备有料斗螺旋加料器,制球机侧面和底部有刮刀和喷雾器,可任意调节造球的大小。优选的,所述粘结剂为亚硫酸盐纸浆废液、废糖蜜、淀粉、叛甲基纤维素中的一种。优选的,其中90%以上在<200网目。优选的,所述制球机造球能力为100kg/h,功率为3.5kw。与现有技术相比,本专利技术的有益效果是:结合牢固程度高、质地均匀,成型快速,还能废物利用。具体实施方式下面将结合本专利技术实施例,对本专利技术实施例中的技术方案进行清楚、完整地描述,显然,所描述的实施例仅仅是本专利技术一部分实施例,而不是全部的实施例。基于本专利技术中的实施例,本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例,都属于本专利技术保护的范围。 ...
【技术保护点】
一种球形煤质活性炭制球工艺,其特征在于:包括如下步骤:(1)将煤全部破碎至<100网目,,水分控制在12%~15%,(2)将煤粉与水分、粘结剂拌均匀后,给入圆盘制球机,其转数为5~25r/min,盘倾角45°‑55°;(3)备有料斗螺旋加料器,制球机侧面和底部有刮刀和喷雾器,可任意调节造球的大小。
【技术特征摘要】
1.一种球形煤质活性炭制球工艺,其特征在于:包括如下步骤:(1)将煤全部破碎至<100网目,,水分控制在12%~15%,(2)将煤粉与水分、粘结剂拌均匀后,给入圆盘制球机,其转数为5~25r/min,盘倾角45°-55°;(3)备有料斗螺旋加料器,制球机侧面和底部有刮刀和喷雾器,可任意调节造球的大小。2.根据权利要求1所...