The invention relates to a ABS box material, in particular to a high scouring and cold resistant ABS box material and a preparation method. ABS resin and maleic anhydride grafted POE, ABS powder, high bromine flame retardant, antistatic agent, inorganic nanoparticles, surface treatment agent, antioxidant, toughening agent and lubricant with high mixing machine according to the formula, a mixture of 5 after 10min at room temperature, the mixture by twin screw extruder extrusion after cooling, drying, cutting, finally after the injection molding injection molding machine molding, preserving the original ABS rigidity, strength and ductility of reinforced material, anti cracking resistance and high impact resistant ABS box material and a preparation method of low temperature.
【技术实现步骤摘要】
一种高抗冲耐寒ABS箱体材料及其制备方法
本专利技术涉及ABS箱体材料，尤其涉及一种高抗冲耐寒ABS箱体材料及其制备方法。
技术介绍
目前市面上的行李箱所用的材质一般都是尼龙料或塑胶材料，包括PP、ABS、PC等。其中，ABS树脂是指丙烯腈、丁二烯-苯乙烯共聚物，ABS树脂是一种强度高、韧性好、易于加工成型的热塑性高分子材料，广泛应用于各类旅行箱。现有技术制备ABS箱体材料过程中，通常在箱体主材ABS材料的基础上加入其它加工助剂，对ABS进行改性，但是由于这些助剂与ABS树脂本身存在物理、化学性质上的差异，改性的同时也破坏了ABS树脂自身在性能方面的优势。另外，ABS树脂容易在高温或高剪切条件下容易分解，且在加工过程中，如果螺杆组合、长径比、工艺控制不合理，容易造成物料降解，严重影响ABS改性材料的力学性能等特点。
技术实现思路
本专利技术的目的在于克服现有技术的不足，提供一种在保留ABS原有的刚性、强度的基础上，增强材料延展性、抗开裂性及耐低温性的高抗冲耐寒ABS箱体材料及其制备方法。本专利技术为实现上述目的而采取的技术方案为：一种高抗冲耐寒ABS箱体材料，其由以下...
【技术保护点】
一种高抗冲耐寒ABS箱体材料，其特征在于：其由以下重量份的组分组成：ABS树脂50‑60份；马来酸酐接枝POE10‑15份；ABS胶粉10‑15份；溴类阻燃剂 5‑10份；抗静电剂2‑4份；无机纳米粒子3‑5份；表面处理剂0.1‑0.2份；抗氧剂0.5‑1份；润滑剂1‑2份；增韧剂1‑2份。
【技术特征摘要】
1.一种高抗冲耐寒ABS箱体材料，其特征在于：其由以下重量份的组分组成：ABS树脂50-60份；马来酸酐接枝POE10-15份；ABS胶粉10-15份；溴类阻燃剂5-10份；抗静电剂2-4份；无机纳米粒子3-5份；表面处理剂0.1-0.2份；抗氧剂0.5-1份；润滑剂1-2份；增韧剂1-2份。2.根据权利要求1所述一种高抗冲耐寒ABS箱体材料，其特征在于：所述无机纳米粒子为纳米碳酸钙、纳米硫酸钡或纳米滑石粉。3.根据权利要求1所述一种高抗冲耐寒ABS箱体材料，其特征在于：所述表面处理剂为硅烷偶联剂、铝酸酯偶联剂或钛酸酯偶联剂。4.根据权利要求1所述一种高抗冲耐寒ABS箱体材料，其特征在于：所述抗氧剂为抗氧化剂1010、抗氧化剂168或抗氧化剂2...
【专利技术属性】
技术研发人员：刘超，周子妍，周应铭，金卓滢，
申请(专利权)人：温州永立箱包有限公司，
类型：发明
国别省市：浙江,33