The invention discloses an ultraviolet light self clean ceramic and a preparation method. The method is as follows: according to the proportion, the kaolin, quartz, dolomite, clay, perovskite, smithsonite and sandstone mixed, according to the quality of raw materials and grinding ball than for 1:3~4 milling, porcelain clay porcelain clay will get; grouting, repair the embryo after firing 1~2h at 400~500 DEG C, and then continue to heat up to 700~900 at time 2~3h, then the warming caused by 1250~1350 C 1~2h ultraviolet self-cleaning firing ceramics. The invention has the effect of ultraviolet and self cleaning, and the ultraviolet lamp on the toilet product made by the invention can have the effect of high efficiency and cleanliness.
【技术实现步骤摘要】
一种紫外光自洁净陶瓷及其制备方法
本专利技术属于洁具卫浴领域,具体涉及一种紫外光自洁净陶瓷及其制备方法。
技术介绍
马桶也叫座便,是大小便用的有盖的桶。马桶的专利技术被称为一项伟大的专利技术,它解决了人自身吃喝拉撒的进出问题。后来又演变为利用虹吸、螺旋虹吸,现在最新的喷射虹吸式和超旋虹吸式等原理的抽水马桶。马桶由于要跟不同使用者在肌肤上有所接触,且马桶的功能是用于排泄,因此卫生状况必须符合要求;现有市面上的马桶都是需要定期清洗。
技术实现思路
本专利技术公开一种紫外光自洁净陶瓷及其制备方法,该陶瓷配合做成的马桶产品上的紫外灯,可有起到高效洁净的效果。本专利技术技术方案如下。一种紫外光自洁净陶瓷,按质量份数计包括:高岭土30~35份石英20~25份白云石15~18份粘土20~25份钙钛矿18~20份菱锌矿10~12份砂岩石10~12份。优选地,按质量份数计包括:高岭土32份石英23份白云石17份粘土23份钙钛矿19份菱锌矿11份砂岩石11份。一种紫外光自洁净陶瓷的制备方法,包括如下步骤:(1)按照配比,将高岭土、石英、白云石、粘土、钙钛矿、菱锌矿和砂岩石混合后,按照原料与研磨球质量比为1:3~4进行球磨,得到瓷泥;(2)将瓷泥进行注浆,修胚后,于400~500℃下烧制1~2h,然后继续升温,于700~900℃下停留2~3h,再升温致1250~1350℃,烧制1~2h即得紫外光自洁净陶瓷。与现有技术相比,本专利技术的优势在于:本专利技术产品具有紫外自洁净的效果,本专利技术陶瓷配合做成的马桶产品上的紫外灯,可有起到高效洁净的效果。具体实施方式以下结合实施例对本专利技 ...
【技术保护点】
一种紫外光自洁净陶瓷,其特征在于,按质量份数计包括:高岭土 30~35份石英 20~25份白云石 15~18份粘土 20~25份钙钛矿 18~20份菱锌矿 10~12份砂岩石 10~12份。
【技术特征摘要】
1.一种紫外光自洁净陶瓷,其特征在于,按质量份数计包括:高岭土30~35份石英20~25份白云石15~18份粘土20~25份钙钛矿18~20份菱锌矿10~12份砂岩石10~12份。2.根据权利要求1所述紫外光自洁净陶瓷,其特征在于,按质量份数计包括:高岭土32份石英23份白云石17份粘土23份钙钛矿19份菱锌矿11份砂岩石11份。3.权利要求1所述紫外...
【专利技术属性】
技术研发人员:谢培东,吴洁新,
申请(专利权)人:广东澳丽泰陶瓷实业有限公司,
类型:发明
国别省市:广东,44