The invention relates to a process for firing furnace Jun emerald green, which comprises the following steps: (1) preparation of raw material, glaze and blue grass material; (2): blank model grouting into blank or manually pull PI can, after the body will be made of the body dry place, after 800 ~ 1000 high temperature drying unglazed, get green body; (3) the glaze: the blank body from top to bottom in the glaze, immersed in two times, and then dry, get a blank; (4) firing the step (3) embryos prepared in the kiln firing 9 ~ 12 hours, temperature from 1200 to 1300, after cooling pit, is finished; the invention has simple process, low production cost, improve the product quality.
【技术实现步骤摘要】
一种翡翠绿炉钧的烧制工艺
本专利技术涉及陶瓷的制作工艺，具体涉及一种翡翠绿炉钧的烧制工艺。
技术介绍
陶瓷的发展史是中华文明史的一个重要的组成部分，中国作为四大文明古国之一，为人类社会的进步和发展做出了卓越的贡献，其中陶瓷的专利技术和发展更具有独特的意义，中国历史上各朝各代有着不同艺术风格和不同技术特点。英文中的"china"既有中国的意思，又有陶瓷的意思，清楚地表明了中国就是"陶瓷的故乡"。早在欧洲人掌握瓷器制造技术一千多年前，汉族就已经制造出很精美的陶瓷器。中国是世界上最早应用陶器的国家之一，而中国瓷器因其极高的实用性和艺术性而备受世人的推崇。从唐花釉瓷到宋钧是个重大飞跃，宋钧所表现出的质感和釉色与唐花釉瓷存在差异，但宋钧传承了唐花釉瓷的蓝色分相，使器物的表面色彩有了很大改善，特别是铜的使用，使材质美发挥至极致，开创了陶瓷美学的新境界。炉钧继承了宋钧在还原气氛中，一氧化碳使釉中的铜、铁、锌等呈色的机理，形成独特的艺术效果，成为钧瓷史上的一朵奇葩，翻开了钧瓷艺术领域中璀璨的一页。炉钧不是普通的透明玻璃釉，区别于普通釉的根本特征在于釉中含有一定数量的可见结晶体，及...
【技术保护点】
一种翡翠绿炉钧的烧制工艺，其特征在于：包括以下步骤：（1） 制备胚料，釉料和草蓝料：所述胚料由以下重量份的原料组成：软土30～50份，花子土8～15份，白土5～12份，砂石1～5份，本药2～4份；所述的釉料由以下重量份的原料组成：草木灰10～60份，长石50～65份，翡翠绿料10～80份，石英5～10份，方解石2～6份，萤石3～8份，熔块30～70份，氧化锡0.1～0.5份，氧化锌0.3～0.8份，氧化铜0.2～0.7份；所述的翡翠绿料由以下重量份的原料组成：晶料 60～80份，铜花10～30份，白砒3～5份，牙硝1～3份；（2）制坯：模型注浆成坯或者手工拉丕均可，制成坯体...
【技术特征摘要】
1.一种翡翠绿炉钧的烧制工艺，其特征在于：包括以下步骤：（1）制备胚料，釉料和草蓝料：所述胚料由以下重量份的原料组成：软土30～50份，花子土8～15份，白土5～12份，砂石1～5份，本药2～4份；所述的釉料由以下重量份的原料组成：草木灰10～60份，长石50～65份，翡翠绿料10～80份，石英5～10份，方解石2～6份，萤石3～8份，熔块30～70份，氧化锡0.1～0.5份，氧化锌0.3～0.8份，氧化铜0.2～0.7份；所述的翡翠绿料由以下重量份的原料组成：晶料60～80份，铜花10～30份，白砒3～5份，牙硝1～3份；（2）制坯：模型注...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。