Ledeburite steel gear differential temperature quenching method, the invention belongs to the technical field of metal heat treatment, ledebrite steel gear differential temperature quenching method, select the preheating temperature of isothermal preheating, then quickly heated to quenching temperature after heat preservation; then cooling temperature after isothermal cooling, the cooling in air, range the preheating temperature is greater than the complete austenitizing temperature critical transition point AC3 or Acm and less than the actual quenching temperature is 50 degrees centigrade, the cooling temperature range is larger than the martensite point Ms and less than Ms+150 DEG C martensite transformation, isothermal quenching temperature after preheating heating to the heating rate is higher than 40 DEG /h, and heated to quenching temperature after the holding time is more than 2h. The quenching method of the gear is more reasonable and can effectively prevent the quenching and cracking.
【技术实现步骤摘要】
莱氏体齿轮钢的差温淬火法
本专利技术属于金属热处理
，涉及一种淬火方法，特别是涉及一种莱氏体齿轮钢的差温淬火法。
技术介绍
中国齿轮工业在“十五”期间得到了快速发展：2005年齿轮行业的年产值由2000年的240亿元增加到683亿元，年复合增长率23.27%，已成为中国机械基础件中规模最大的行业。就市场需求与生产规模而言，中国齿轮行业在全球排名已超过意大利，居世界第四位。齿轮及其齿轮产品是机械装备的重要基础件，绝大部分机械成套设备的主要传动部件都是齿轮传动。随着国民经济的高速发展，全行业年销售总额已突破千亿元，形成了企业多元并存、共同发展的行业格局。其中，龙头企业、骨干企业已成为推动行业管理水平、产品技术质量水平和自主创新能力提升的重要力量，为把我国从齿轮制造大国建设成为齿轮制造强国做出了突出贡献。根据(中国齿轮行业产销需求预测与转型升级分析报告)显示中国齿轮传动行业在“十一五”期间得到了快速发展，2005-2010年中国齿轮行业的工业总产值逐年增加，且同比增幅均在20%以上。2010年整个齿轮产业实现工业总产值946.35亿元，齿轮全行业市场需求超过140...
【技术保护点】
莱氏体齿轮钢的差温淬火法，其特征在于：选取预热温度进行等温预热，然后快速加热至淬火温度后保温；接着选取冷却温度进行等温冷却，最后再在空气中冷却，预热温度的范围为大于完全奥氏体化温度临界转变点AC3或Acm且小于实际淬火温度50℃，冷却温度的范围为大于马氏体转变点Ms且小于马氏体转变点Ms+150℃，等温预热后加热至淬火温度的升温速度为大于40℃/h，且加热至淬火温度后保温时间大于2h。
【技术特征摘要】
1.莱氏体齿轮钢的差温淬火法，其特征在于：选取预热温度进行等温预热，然后快速加热至淬火温度后保温；接着选取冷却温度进行等温冷却，最后再在空气中冷却，预热温度的范围为大于完全奥氏体化温度临界转变点AC3或Acm且小于实际淬火温度50℃，冷却温度的范围为大于马氏体转变点Ms且小于马氏体转变点Ms+150℃，等温预热后加热至淬火温度的升温速度为大于40℃/h，且加热至淬火温度后保温时间大于2h。2.如权利要求1所述的莱氏体齿轮钢的差温淬火法加工获得...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。