The invention discloses an automobile interior board and its preparation method, its preparation method by sheet extruder rolled into sheet, which comprises the following formula quality content components: PP 100, inorganic flame retardant 5 - 20, 5 - 50, glass light stabilizer 0.01 ~ 0.5. The automobile interior trim plate has obvious improvement in mechanical strength and flame retardancy under the premise of ensuring lightweight. The size stability and anti-aging effect are better, and the zero formaldehyde standard is achieved. The preparation method is simple and easy to achieve industrialization. It can be coated or pasted on the outer surface of the board to enhance the aesthetics, and it can be applied to the field of automotive interior panels.
【技术实现步骤摘要】
一种汽车内饰板及其制备方法
本专利技术涉及装饰板材领域,尤其涉及一种汽车内饰板及其制备方法。
技术介绍
汽车内饰板大多为聚氯乙烯、沥青、木塑等材质。由于环境资源的日益短缺,人们对于装饰板材的美观及轻量化要求越来越高,所以木塑材质的装饰板材越来越受到大家的青睐。但木塑板材或多或少都会含有一定的甲醛,对大气环境以及人体健康存在严重的健康威胁。本专利技术涉及一种新型的汽车内饰板的制备,该方法在传统高分子材料里掺杂玻纤,制备复合板材用作汽车内饰板。本专利技术克服了木塑板材含甲醛的缺点。并通过拉力测试,SEM等测试表明该材料综合性能稳定,且在汽车内饰板材领域有很好的应用前景。
技术实现思路
有鉴于此,本专利技术的目的在于通过将聚丙烯与玻纤进行共混来制备无甲醛装饰板,并能有效应用于工业化生产中。基于上述目的,本专利技术制备的汽车内饰板,由以下原料按照各自重量份配比组成:聚丙烯(PP)100份,无机阻燃剂5~20份,玻纤5~50份,光稳定剂0.01~0.5份。优选的,所述的玻纤为无碱玻璃纤维短切丝,其长度为3~15mm。优选的,所述的无机阻燃剂为氢氧化镁(镁粉)、氢氧化铝等阻燃剂中的一种或多种复配。为解决上述技术问题,本专利技术提出了如下技术方案,其包括如下步骤:步骤一:按既定用量称取各原料,即聚丙烯100质量份、无机阻燃剂5~20质量份,玻纤5~50质量份,光稳定剂0.01~0.5质量份;步骤二:将称取的聚丙烯、无机阻燃剂、玻纤、光稳定剂置于高速混合机中混合3~15min;步骤三:步骤二中混合后的物料于板材挤出机中挤出压延成板材。从上面所述可以看出,根据本专利技术提供的制 ...
【技术保护点】
一种汽车内饰板,其特征在于,包括如下质量百分比的各组份:
【技术特征摘要】
1.一种汽车内饰板,其特征在于,包括如下质量百分比的各组份:。2.根据权利要求1所述的汽车内饰板,其特征在于,所述的无机阻燃剂为氢氧化镁、氢氧化铝等阻燃剂中的一种或多种复配。3.根据权利要求1所述的汽车内饰板,其特征在于,所述的玻纤为无碱玻璃纤维短切丝,其长度为3~15mm。4.根据权利要求1所述的汽车内饰板,其特征在于,所述的光稳定剂包括光屏蔽剂、紫外线吸收剂、淬灭剂或自由基捕获剂中的一种或多种复配。5.根据...
【专利技术属性】
技术研发人员:杨先刚,
申请(专利权)人:无锡市天聚科技有限公司,
类型:发明
国别省市:江苏,32
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。