本发明专利技术公开了一种复合陶瓷材料及其制备的电饭煲内胆，该复合材料由以下重量份原料组成：氮化铝50～70份、Y2O3 1～2份、La2O3 2～3份、SiO2 10～15份、B2O3 10～20份、纳米TiO2 1～1.5份。电饭煲内胆是由以下步骤制成：1)称取配方量的各原料；2)将上述原料经混料机混合均匀，充填入模型中，在1400～1500℃的高温熔块炉熔化，倒入模具中成型，即得陶瓷内胆。本发明专利技术能显著提高氮化铝陶瓷内胆的热传导率，大大节约能耗。

A composite ceramic material and a prepared electric cooker inner bladder

The invention discloses an electric rice cooker liner composite ceramic material and its preparation, the composite material by weight of raw materials: aluminum nitride 50 - 70, Y2O3 1 - 2, La2O3 - 3, SiO2 2 10 - 15, B2O3 - 20, 10 nm TiO2 1 ~ 1.5. Rice cooker liner is made by the following steps: 1) said the amount of raw material formulation; 2) the raw materials by mixing machine mixing, filling model, in high temperature 1400 to 1500 DEG C melting frit furnace, poured into the mold, the ceramic liner. The invention can significantly improve the thermal conductivity of the aluminum nitride ceramic inner bladder, and greatly save energy consumption.

【技术实现步骤摘要】
一种复合陶瓷材料及其制备的电饭煲内胆
本专利技术属于陶瓷材料领域，具体涉及一种复合陶瓷材料以及制备的电饭煲内胆。
技术介绍
电饭煲是大众的必须日用品，目前市场上的电饭煲内胆主要采用铝合金材料。铝合金材料具有质量轻、热传导性好等优点，采用各种涂覆技术后还能不粘锅。但由于机械作用易使得涂层的化学材料或铝元素进入人体，对人体健康造成危害。如将陶瓷内胆应用于电饭煲中取代普通的铝合金内胆，可克服铝胆易粘锅、不易刷洗、铝元素对人体有害等一系列缺点。然而陶瓷内胆也存在一些劣势，加热慢，导热率低，传热不均，常发生煮饭半生不熟的问题。因此，研究一种传热效率高，节能降耗，使用寿命长的陶瓷内胆迫在眉睫。
技术实现思路
本专利技术要解决的技术问题是提供一种提高热传导率的电饭煲陶瓷内胆的制备方法，该方法制得的陶瓷内胆热传导率高，大大节省能耗。本专利技术提供的技术方案是电饭煲陶瓷内胆的制备方法，包括以下步骤：1)称取以下重量份的原料：氮化铝50～70份、Y2O31～2份、La2O32～3份、SiO210～15份、B2O310～20份、纳米TiO21～1.5份；2)将上述原料经混料机混合均匀，充填入模型中，在1400本文档来自技高网...

【技术保护点】
一种复合陶瓷材料，其特征在于：由以下重量份原料组成：氮化铝50～70份、Y2O3 1～2份、La2O3 2～3份、SiO2 10～15份、B2O3 10～20份、纳米TiO2 1～1.5份。

【技术特征摘要】
1.一种复合陶瓷材料，其特征在于：由以下重量份原料组成：氮化铝50～70份、Y2O31～2份、La2O32～3份、SiO210～15份、B2O310～20份、纳米TiO21～1.5份。2.根据权利要求1所述的复合陶瓷材料，其特征在于：所述氮化铝是采用Al2O3粉末与炭黑粉末经过球磨混合，在流动的氮气气氛中以氧化钙为催化剂，在1500～1700℃下反应生成；反应完成后，在700～800℃的干燥空气中进行脱碳处理。3.根据权利要求2所述的复合陶瓷材料，其特征在于：所述Al2O3粉末中阳离子杂质含量≤0.02％，其中硅和...

【专利技术属性】
技术研发人员：孙继旋，张科研，甘冠蓝，王宁，钟恒成，王刚，张庆峰，
申请(专利权)人：钦州学院，
类型：发明
国别省市：广西,45