一种氯化锌连续法生产活性炭的方法技术

本发明专利技术公开了一种氯化锌连续法生产活性炭的方法，包括如下步骤（1）选取6‑40目的木屑，干燥至含水率为15‑20%；（2）氯化锌溶液中加入盐酸，形成混合溶液；（3）将木屑和步骤（2）溶液捏合；（4）将步骤（3）捏合物加入回转炉活化；（5）漂洗活化产物，离心脱水、干燥、磨粉，并最后装袋。该发明专利技术的有益效果在于：其氯化锌消耗量低，生产环境清洁，大大降低生产成本，最主要保护了环境，实现了清洁生产。

A method of continuous production of activated carbon by zinc chloride

The invention discloses a method for producing a continuous zinc chloride activated carbon method, comprising the steps of (1) from 6 to 40 sawdust, drying to 15 moisture content 20%; (2) adding hydrochloric acid solution of zinc chloride, the formation of a mixed solution; (3) the sawdust and step (2) solution pinch; (4) the step (3) added the kneading rotary furnace activation; (5) rinsing activated products, centrifugal dewatering, drying, milling, and finally packing. The invention has the beneficial effect that the consumption of zinc chloride is low, the production environment is clean, the production cost is largely reduced, the environment is protected, and the cleaner production is realized.

【技术实现步骤摘要】
一种氯化锌连续法生产活性炭的方法
本专利技术涉及吸附剂
，具体为一种氯化锌连续法生产活性炭的方法。
技术介绍
活性炭是一种黑色多孔的固体炭质，由煤通过粉碎、成型或用均匀的煤粒经炭化、活化生产。主要成分为碳，并含少量氧、氢、硫、氮、氯等元素。普通活性炭的比表面积在500～1700m²/g间。具有很强的吸附性能，为用途极广的一种工业吸附剂。传统化学法制造活性炭的缺点是活化剂消耗大，回收率低，产生的废水废气对环境造成危害，急需一种新的制备方法。
技术实现思路
本专利技术的目的在于提供一种氯化锌连续法生产活性炭的方法，以解决上述
技术介绍
中提出的问题。为实现上述目的，本专利技术提供如下技术方案：一种氯化锌连续法生产活性炭的方法，包括如下步骤（1）选取6-40目的木屑，干燥至含水率为15-20%；（2）氯化锌溶液中加入盐酸，形成混合溶液；（3）将木屑和步骤（2）溶液捏合；（4）将步骤（3）捏合物加入回转炉活化；（5）漂洗活化产物，离心脱水、干燥、磨粉，并最后装袋。优选的，所述步骤（1）中，木屑采用120-150摄氏度的热风干燥。优选的，所述步骤（2）中，氯化锌溶液浓度为50%。优选的，所述步骤本文档来自技高网...

【技术保护点】
一种氯化锌连续法生产活性炭的方法，其特征在于：包括如下步骤（1）选取6‑40目的木屑，干燥至含水率为15‑20%；（2）氯化锌溶液中加入盐酸，形成混合溶液；（3）将木屑和步骤（2）溶液捏合；（4）将步骤（3）捏合物加入回转炉活化；（5）漂洗活化产物，离心脱水、干燥、磨粉，并最后装袋。

【技术特征摘要】
1.一种氯化锌连续法生产活性炭的方法，其特征在于：包括如下步骤（1）选取6-40目的木屑，干燥至含水率为15-20%；（2）氯化锌溶液中加入盐酸，形成混合溶液；（3）将木屑和步骤（2）溶液捏合；（4）将步骤（3）捏合物加入回转炉活化；（5）漂洗活化产物，离心脱水、干燥、磨粉，并最后装袋。2.根据权利要求1所述的一种氯...

【专利技术属性】
技术研发人员：陈天烨，
申请(专利权)人：江苏科力特环保科技有限公司，
类型：发明
国别省市：江苏,32