The present invention provides a rubber protective clothing and fabric, including skeleton material and adhesive material, which is characterized in that the skeleton material for synthetic fiber, and attached materials for rubber material, and the rubber is composed of rubber matrix, plasticizer, curing agent, active agent, accelerator, reinforcement agent, the rubber matrix for Ding Ji chlorinated rubber and butadiene rubber blends, the Ding Ji of chlorinated rubber and butadiene rubber composition ratio is 60:40~80:20. The invention brushing the rubber mixture on the synthetic fiber of the skeleton material, ingeniously combines the characteristics of the two, and produces a protective clothing, which is capable of both flame-retardant, anti-virus and mechanical properties. It is also comfortable to wear, simple in production process, easy to implement and widely applied.
【技术实现步骤摘要】
一种并用橡胶防护服面料
本专利技术涉及个体防护服面料领域，具体涉及一种并用橡胶防护服面料。技术背景在国内，防护服面料多是直接将纺丝液制成具备防护功能的原纺材料，经纺织加工，得到具有多重防护性能的功能材料，但关于以并用橡胶为基体材料，制备具有阻燃、防毒、舒适性能好的特种高分子防护面料的生产方法、工艺参数、生产设备等的相关报道和专利较少，对并用橡胶为基体的特种高分子橡塑防护面料的防护机理、制备工艺研究至今还不系统、不深入。
技术实现思路
为了解决上述技术问题本专利技术提供一种并用橡胶防护服面料。本专利技术的技术方案是：一种并用橡胶防护服面料，包括骨架材料和附着材料，所述骨架材料为合成纤维，附着材料为并用橡胶材料，所述并用橡胶组成和质量分数为：橡胶基体100份，增塑剂25-35份、活性剂2-8份、硫化剂6-9份，促进剂1-3份，补强剂30-45份，所述橡胶基体为氯化丁基橡胶和顺丁橡胶共混物，所述氯化丁基橡胶和顺丁橡胶质量比为60：40～80：20。方案进一步地，所述补强剂为白炭黑。方案进一步地，所述促进剂为TMTD和/或DM。一种并用橡胶防护服面料的制备方法是：将氯化丁...
【技术保护点】
一种并用橡胶防护服面料，包括骨架材料和附着材料，其特征在于，所述骨架材料为合成纤维，附着材料为并用橡胶材料，所述并用橡胶组成和质量分数为：橡胶基体100份，增塑剂25‑35份、活性剂2‑8份、硫化剂6‑9份，促进剂1‑3份，补强剂30‑45份，所述橡胶基体为氯化丁基橡胶和顺丁橡胶共混物，所述氯化丁基橡胶和顺丁橡胶组份比为60：40~80：20。
【技术特征摘要】
1.一种并用橡胶防护服面料，包括骨架材料和附着材料，其特征在于，所述骨架材料为合成纤维，附着材料为并用橡胶材料，所述并用橡胶组成和质量分数为：橡胶基体100份，增塑剂25-35份、活性剂2-8份、硫化剂6-9份，促进剂1-3份，补强剂30-45份，所述橡胶基体为氯化丁基橡胶和顺丁橡胶共混物，所述氯化丁基橡胶和顺丁橡胶组份比为60：40~80：20。2.根据权利要求1所述的一种并用橡胶防护服面料，其特征在于，所述补强剂为白炭黑。3.根据权利要求2所述的一种并用橡胶防护服面料，其特征在于，所述促进剂为TMTD和/或DM。4.根据权利要求3所述的一种...