本发明专利技术公开了属于建筑材料制备技术领域的一种建筑节能墙板及其制备方法。由如下重量份数的原料制成：水泥130‑180份，植物纤维20‑35份，高岭土30‑45份，白炭黑3‑5份，防水剂3‑5份，粘结剂3‑8份，高分子化合物10‑30份，水100‑200份。本发明专利技术的节能环保的板材制备方法简单，能源消耗少，制备的板材抗压和抗折性能好，长时间使用，性能不衰减，应用领域广，适合大规模工业化生产。

A kind of building energy saving wallboard

The invention discloses a building energy saving wallboard and a preparation method belonging to the technical field of building material preparation. Made from the following raw materials in parts by weight: 130 cement plant fiber 20 180 copies, 35 copies, 45 copies of 30 kaolin, white carbon black 3 5 copies, 5 copies of 3 waterproof agent, binder 3 8 copies, 10 polymer compound 30, water 100 200. The energy-saving and environment-friendly plate preparation method is simple, energy consumption is less, the prepared sheet has good compressive and flexural performance, long time use, no attenuation of performance and wide application area, and is suitable for large-scale industrial production.

【技术实现步骤摘要】
一种建筑节能墙板
本专利技术属于建筑材料制备
，具体涉及一种建筑节能墙板及其制备方法。
技术介绍
传统的墙板是由墙和楼板组成承重体系的房屋结构。墙既作承重构件，又作房间的隔断，是居住建筑中最常用且较经济的结构形式。缺点是室内平面布置的灵活性较差，为克服这一缺点，目前正在向大开间方向发展。墙板结构多用于住宅、公寓、也可用于办公楼、学校等公用建筑。墙板结构的承重墙可用砖、砌块、预制或现浇混凝土做成。专利200610009662.0公开了一种轻质墙板，所用原料按重量配比，配料为：粉煤灰30～40份、氧化镁15～25份、氯化镁10～20份、石灰或水泥3～10份、石膏5～15份、草木粉5～15份、玻璃丝1～5份；外加剂为：硫酸亚铁0.5～1.5份、草酸0.5～1.5份、磷酸三钠0.1～1份、六偏磷酸钠0.1～1份、聚醋酸乙烯1～2份；将氧化镁加水搅拌均匀，配制成波美度为18～25的溶液后，加入外加剂搅拌均匀，再加入粉煤灰、氯化镁、石灰或水泥、石膏、草木粉搅拌均匀制成浆料，向模具中铺装浆料，浆料铺至一半厚度时环形抛撒玻璃丝，再铺装浆料，捣实成型，脱模、干燥后而成。该墙板虽然质量轻，但是，抗本文档来自技高网...

【技术保护点】
一种建筑节能墙板，其特征在于，由如下重量份数的原料制成：水泥130‑180份，植物纤维20‑35份，高岭土30‑45份，白炭黑3‑5份，防水剂3‑5份，粘结剂3‑8份，高分子化合物10‑30份，水100‑200份。

【技术特征摘要】
1.一种建筑节能墙板，其特征在于，由如下重量份数的原料制成：水泥130-180份，植物纤维20-35份，高岭土30-45份，白炭黑3-5份，防水剂3-5份，粘结剂3-8份，高分子化合物10-30份，水100-200份。2.根据权利要求1所述建筑节能墙板，其特征在于，所述高分子化合物为聚丙氨酸，聚谷氨酸，聚赖氨酸，乙烯-α，β-不饱和羧酸共聚物，1-丁烯-丙烯共聚物中的一种或一种以上。3.根据权利要求1所述建筑节能墙板，其特征在于，所述粘结剂为焦油渣，丙烯睛-丁二烯-苯乙烯共聚物，硅溶胶，邻苯二甲酸二辛酯中的一种或一种以上。4.根据权利要求1所述建筑节能墙板，其特征在于，所述防水剂为一甲基三氯硅烷，羟基树脂，十二水硫酸铝钾，椰油...