一种凹印版辊氯化铜预腐蚀工艺制造技术

本发明专利技术涉及一种凹印版辊氯化铜预腐蚀工艺，包括将激光雕刻版辊先后用混合液和铬酐溶液进行预腐蚀的步骤；混合液由铬酐溶液和氯化铜溶液混合制得。与现有技术相比，本发明专利技术不使用三氯化铁，从而避免使用三氯化铁所带来的弊端；氯化铜溶液可以来自于后续的腐蚀工艺中的氯化铜腐蚀液，从而实现腐蚀液的高效利用，也节约了成本和生产工艺；本发明专利技术的工艺对产品后续质量无影响，能够保证产品质量。

A gravure roller of copper corrosion process

The invention relates to a gravure roller of copper corrosion process, including laser engraving and successively pre corrosion by using mixed liquid and chromic anhydride solution steps; mixed liquid by chromic acid solution and copper chloride solution mixing. Compared with the prior art, the invention does not use ferric chloride, so as to avoid the drawbacks caused by the use of ferric chloride; cupric chloride etching solution from copper chloride solution in the subsequent etching process, so as to achieve efficient use of corrosive liquid, but also saves the cost and production process; the process of the invention has no effect on the follow-up to product quality. To ensure the quality of products.

【技术实现步骤摘要】
一种凹印版辊氯化铜预腐蚀工艺
本专利技术涉及一种凹印版辊预腐蚀工艺，尤其是涉及一种凹印版辊氯化铜预腐蚀工艺。
技术介绍
目前铜辊制版技术主要有电子雕刻及激光雕刻两种生产方式，激光雕刻由于其网型深浅的任意性，已经大面积使用，先在钢棍上镀铜，然后挂胶，再进行激光雕刻，之后通过蚀刻，得到凹印版辊，蚀刻时先进行预腐蚀，再进行腐蚀。由于预腐蚀和腐蚀普遍采用三氯化铁，例如中国专利CN104626786A，其污染较为严重，虽然CN1660704A公开一种凹版印刷制版废液的处理工艺，能够提取Cu，并实现废液循环利用，但是这无疑增加了工艺的复杂性和生产成本。况且，采用三氯化铁进行预腐蚀时剧烈的反应导致横竖笔画粗细差别严重，大面积版面色差严重，局部图案腐蚀严重不均，人工控制难度很大等问题。目前有公司采用氯化铜代替三氯化铁作为腐蚀工序的腐蚀剂，但是在预腐蚀工序，还是沿用三氯化铁进行预腐蚀，例如中国专利CN103522731A，这种工艺照样不能避免三氯化铁的使用，照样存在使用三氯化铁时的弊端。
技术实现思路
本专利技术的目的就是为了克服上述现有技术存在的缺陷而提供一种凹印版辊氯化铜预腐蚀工艺。本专利技术的目的可本文档来自技高网...

【技术保护点】
一种凹印版辊氯化铜预腐蚀工艺，其特征在于，包括将激光雕刻版辊先后用混合液和铬酐溶液进行预腐蚀的步骤；所述的混合液由铬酐溶液和氯化铜溶液混合制得。

【技术特征摘要】
1.一种凹印版辊氯化铜预腐蚀工艺，其特征在于，包括将激光雕刻版辊先后用混合液和铬酐溶液进行预腐蚀的步骤；所述的混合液由铬酐溶液和氯化铜溶液混合制得。2.根据权利要求1所述的一种凹印版辊氯化铜预腐蚀工艺，其特征在于，包括以下步骤：(1)在激光雕刻版辊转动过程中，用混合液沿激光雕刻版辊轴向方向刷版两个来回，彻底冲水；(2)在激光雕刻版辊转动过程中，用铬酸溶液沿激光雕刻版辊轴向方向刷版一个来回，彻底冲水，完成预腐蚀，并尽快入氯化铜腐蚀槽中。3.根据权利要求1或2所述的一种凹印版辊氯化铜预腐蚀工艺，其特征在于，所述的铬酐溶液的波美度为8～10，氯化铜溶液的波美度为28～31，混合液中铬酐溶...

【专利技术属性】
技术研发人员：王刚，
申请(专利权)人：山西运城制版集团上海企业发展有限公司，
类型：发明
国别省市：上海,31