The invention discloses a ship metal surface acid lotion, which is characterized in that; the component comprises the following components by weight percentage: 0.8mol/L of dilute sulfuric acid or hydrochloric acid of 45 copies, 2.9 copies of Aminothiourea, Carboxycellulose salt 14, rosin amine polyoxyethylene ether 12, surfactant OP 10, benzo three triazole 30 copies, 14 copies of 7 copies of imidazoline, potassium iodide. The invention of the products prepared to remove the oxide rust metal surface, through further reaction with dilute acid steel matrix, in order to prevent the excessive corrosion of metal by dilute acid, carboxyl cellulose salt, rosin amine polyoxyethylene ether, OP surfactant and benzo triazole three, the activation energy change corrosion chemical process or cathodic reaction the anodic reaction, and drag the cathode and anode reaction by thiosemicarbazide, imidazoline and iodide on the steel surface to form a seal protective film.
【技术实现步骤摘要】
一种船舶金属表面酸洗剂
本专利技术涉及一种金属防护剂，具体涉及一种船舶金属表面酸洗剂及其制备方法。
技术介绍
金属与海水发生电化学反应而损耗和变质。海水中金属的电化学腐蚀是由于金属表面的电化学不均匀性引起的。这种不均匀性可由金属本身(例如晶界、夹杂等)或金属表面不同部位上介质的变化(例如氧浓差等)而产生。碳钢是开发海洋资源设施中应用最广泛的结构材料。人们对碳钢在海水中的腐蚀行为进行过相当详细的研究。广泛的挂片试验表明，碳钢在海水中的平均腐蚀速度为0.05－0.13毫米/年，而点蚀速度可达平均年腐蚀率的10倍。影响钢在海水中腐蚀速度的主要因素是对钢表面氧的供给速度，此外还有温度、流速、污损生物、石灰质垢、污染以及钢结构的焊接、应力等，也是腐蚀速度的影响因素。所以市场迫切需要有一种金属表面酸洗剂来缓解金属表面腐蚀现象。
技术实现思路
专利技术目的：为了克服现有技术中存在的不足，本专利技术提供一种船舶金属表面酸洗剂。本专利技术还提供了上述酸洗剂的制备方法。技术方案：为实现上述目的，本专利技术提供一种船舶金属表面酸洗剂，其组分按重量百分比由以下成分组成：0.8mol/L的稀硫...
【技术保护点】
一种船舶金属表面酸洗剂，其特征在于；其组分按重量百分比由以下成分组成：0.8mol/L的稀硫酸或者稀盐酸48份，氨基硫脲3.2份，羧基纤维素盐15份，松香胺聚氧乙烯醚12份，OP表面活性剂15份，苯并三氮唑35份，咪唑啉15份，碘化钾9份。
【技术特征摘要】
1.一种船舶金属表面酸洗剂，其特征在于；其组分按重量百分比由以下成分组成：0.8mol/L的稀硫酸或者稀盐酸48份，氨基硫脲3.2份，羧基纤维素盐15份，松香胺聚氧乙烯醚12份，OP表面活性剂15份，苯并三氮唑35份，咪唑啉15份，碘化钾9份。2.根据权利要求1所述的一种船舶金属表面酸洗剂，其特征在...
【专利技术属性】
技术研发人员：许国华，
申请(专利权)人：南通如港船舶配套机械有限公司，
类型：发明
国别省市：江苏,32