The invention relates to an organosilicon sealant, which belongs to the technical field of building joint. The invention firstly uses two methyl hydrogen chlorosilane and two methyl siloxane, distilled water and platinum black into a reactor, using nitrogen gas to discharge the air in the reactor, after the reaction, adding methyl trimethoxysilane, collecting the liquid after cooling treatment, namely adding liquid, then aluminum nitrate and methacrylic acid two dimethylamino ethyl ester into the container, stir in adding ammonium bicarbonate after heating, filtering, collecting a residue, then the residue to dry, dry collection of calcining and sieving to the filler particles, and the hydroxyl terminated poly two methyl siloxane and add liquid mixing, silicone the sealant obtained by the invention has excellent mechanical properties, good heat resistance.
【技术实现步骤摘要】
一种有机硅密封胶
本专利技术涉及一种有机硅密封胶，属于建筑接缝
技术介绍
有机硅密封胶是一类通用的密封材料，使用时胶料从软管或封筒内挤出，接触空气中的湿气后交联成弹性体，胶料的组分包括反应性基础聚合物(基胶)、交联剂、催化剂、填料、增塑剂以及其它功能型添加剂。有机硅硅密封胶具有优异的耐紫外、抗臭氧、耐热，以及低温柔性等物理化学性能，对基材粘接性好、施工方便、固化速度快，是广泛应用于汽车、家电等装配制造中重要的工艺材料之一，在电子、工业行业等方面起着重要作用。目前各种电子及工业行业对于产品的使用寿命要求越来越长，与此同时目前越来越多的电子器件需要在户外环境下使用，因此对于应用到这些行业中的有机硅密封胶而言，除了要求密封胶必须要具备良好的机械及粘接性能之外，对于密封胶的耐候性也提出了更高的要求，尤其是耐湿热性方面。目前市面上许多有机硅密封胶耐湿热性不理想，从而导致胶的力学性能会大幅下降，甚至完全丧失强度的问题。因此，亟待寻找一种耐湿热性能好，胶的力学性能家的有机硅密封胶。
技术实现思路
本专利技术主要解决的技术问题是：针对传统有机硅密封胶的耐湿热性不理想，从而导...
【技术保护点】
一种有机硅密封胶，其特征在于：包括以下重量份数的组份，60～70份端羟基聚二甲基硅氧烷、25～30份添加液及6～9份填充颗粒。
【技术特征摘要】
1.一种有机硅密封胶，其特征在于：包括以下重量份数的组份，60～70份端羟基聚二甲基硅氧烷、25～30份添加液及6～9份填充颗粒。2.根据权利要求1所述的一种有机硅密封胶，其特征在于：所述添加液的原料包括按重量份数计的如下组份，40～45份甲基氢二氯硅烷、30～35份二甲基硅氧烷、20～25份蒸馏水、8～11份甲基三甲氧基硅烷及5～7份铂黑。3.根据权利要求1或2所述的一种有机硅密封胶，其特征在于：所述添加液的制备，包括如下制备步骤：（1）将40～45份甲基氢二氯硅烷、30～35份二甲基硅氧烷、20～25份蒸馏水及5～7份铂黑放入反应釜中，使用氮气保护，在103～112℃下搅拌混合，再使用氢气将反应釜中气体排出，加入8～11份甲基三甲氧基硅烷，降温至60～70℃，反应1～2h；（2）在反应结束后进行出料，收集出料物，将出料...
【专利技术属性】
技术研发人员：郜九宏，宋昊，赵成浩，
申请(专利权)人：常州彤骉贸易有限公司，
类型：发明
国别省市：江苏,32