一种五金耐腐蚀涂层制造技术

本发明专利技术涉及五金零部件领域，尤其是一种五金耐腐蚀涂层。其原料按重量份计为：聚酰亚胺15～25份、阴离子丙烯酸树脂10～20份、肌醇六磷酸酯5～10份、纳米二氧化钛1～3份、氧化锌粉2～5份、滑石粉3～8份、羟乙基纤维素4～8份、改性氢化蓖麻油2～5份、有机溶剂20～40份。可以有效实现对五金产品的防护。具有防锈、耐腐蚀功能。同时耐候性、耐磨性、耐冲击性、防霉性强。

A kind of hardware corrosion resistant coating

The invention relates to the field of hardware parts, in particular to a kind of hardware corrosion resistant coating. The raw materials by weight: 15 to 25 portions of polyimide and anionic acrylic resin 10 ~ 20, 5 ~ six phosphate inositol 10, 1 to 3 portions of nano titanium dioxide zinc oxide, 2 - 5, 3 - 8, talcum powder 4 ~ 8, hydroxyethyl cellulose modified castor oil 2 - 5, 20 to 40 parts of organic solvent. Can effectively realize the protection of hardware products. It has the function of rust prevention and corrosion resistance. At the same time, the weather resistance, abrasion resistance, impact resistance, mildew resistance are strong.

【技术实现步骤摘要】
一种五金耐腐蚀涂层
本专利技术涉及五金零部件领域，尤其是一种五金耐腐蚀涂层。
技术介绍
五金：传统的五金制品，也称“小五金”。指金、银、铜、铁、锡五种金属。经人工加工可以制成刀、剑等艺术品或金属器件。现代社会的五金更为广泛，例如五金工具、五金零部件、日用五金、建筑五金以及安防用品等。小五金产品大都不是最终消费品。现有的五金产品在长久使用后，容易发生生锈的状况，影响使用寿命与使用安全。
技术实现思路
为解决上述问题，本专利技术提供了一种五金耐腐蚀涂层，可以实现对五金产品的防护。为了实现上述目的，本专利技术所采用以下技术方案，一种五金耐腐蚀涂层，其原料按重量份计为：聚酰亚胺15～25份、阴离子丙烯酸树脂10～20份、肌醇六磷酸酯5～10份、纳米二氧化钛1～3份、氧化锌粉2～5份、滑石粉3～8份、羟乙基纤维素4～8份、改性氢化蓖麻油2～5份、有机溶剂20～40份。进一步，一种五金耐腐蚀涂层，其原料按重量份计为：聚酰亚胺20份、阴离子丙烯酸树脂15份、肌醇六磷酸酯8份、纳米二氧化钛2份、氧化锌粉3份、滑石粉5份、羟乙基纤维素6份、改性氢化蓖麻油4份、有机溶剂30份。采用本专利技术所述的涂层，可以本文档来自技高网...

【技术保护点】
一种五金耐腐蚀涂层，其特征在于，其原料按重量份计为：聚酰亚胺15～25份、阴离子丙烯酸树脂10～20份、肌醇六磷酸酯5～10份、纳米二氧化钛1～3份、氧化锌粉2～5份、滑石粉3～8份、羟乙基纤维素4～8份、改性氢化蓖麻油2～5份、有机溶剂20～40份。

【技术特征摘要】
1.一种五金耐腐蚀涂层，其特征在于，其原料按重量份计为：聚酰亚胺15～25份、阴离子丙烯酸树脂10～20份、肌醇六磷酸酯5～10份、纳米二氧化钛1～3份、氧化锌粉2～5份、滑石粉3～8份、羟乙基纤维素4～8份、改性氢化蓖麻油2～5份、有机溶剂2...