The invention relates to a preparation method of enhanced environmental protection of insulation materials, the enhanced environmental protection insulation material is composed of the following components in part by weight: 6 HRB 80 resin 120, alkali free glass fiber wire 20 40 and 8 polypropylene fiber 12 copies, 6 copies of 4 solubilizer nanoporous silica, 16 24, two 15 and 5 methyl silicone oil antioxidant 6 10. The advantages of the invention are as follows: through the preparation method of the enhanced environmental protection insulating material, the prepared insulating material has high mechanical strength, good heat resistance and good breakdown resistance, and is an environment-friendly insulating material with excellent comprehensive performance.
【技术实现步骤摘要】
一种增强型环保绝缘材料的制备方法
本专利技术涉及绝缘材料
，特别涉及一种增强型环保绝缘材料的制备方法。
技术介绍
聚酯由于其优异的成型加工性、电绝缘性和耐热性能被广泛应用于电子、电器和家电等行业。近年来，随着社会对环境问题的高度关注，聚酯中的环境友好型聚对苯二甲酸丁二醇酯（PBT）被广泛用于电气绝缘材料领域。电气领域通常指高温、高压环境，而普通的PBT材料因机械强度、耐热性和介电性能欠佳，在上述环境中易发生击穿破坏。
技术实现思路
本专利技术要解决的技术问题是提供一种能够满足高温、高压环境使用要求的增强型环保绝缘材料的制备方法。为解决上述技术问题，本专利技术的技术方案为：一种增强型环保绝缘材料的制备方法，其创新点在于：所述制备方法包括如下步骤：（1）按重量份配比准确称取各原料备用：HRB-6树脂80-120份、无碱玻璃纤维丝20-40份、聚丙烯纤维8-12份、增溶剂4-6份、纳米多孔二氧化硅16-24份、二甲基硅油5-15份和抗氧剂6-10份；（2）将HRB-6树脂、增溶剂、纳米多孔二氧化硅和抗氧剂依次加入密炼机中，以100转/min的转速搅拌混合20min，然...
【技术保护点】
一种增强型环保绝缘材料的制备方法，其特征在于：所述制备方法包括如下步骤：（1）按重量份配比准确称取各原料备用：HRB‑6树脂80‑120份、无碱玻璃纤维丝20‑40份、聚丙烯纤维8‑12份、增溶剂4‑6份、纳米多孔二氧化硅16‑24份、二甲基硅油5‑15份和抗氧剂6‑10份；（2）将HRB‑6树脂、增溶剂、纳米多孔二氧化硅和抗氧剂依次加入密炼机中，以100转/min的转速搅拌混合20min，然后将密炼机升温至190℃，在搅拌的同时从加料斗依次加入无碱玻璃纤维丝、聚丙烯纤维和二甲基硅油，密炼10～20min，使混合料全部混匀，降温冷却后出料，并切割成小碎块；（3）将步骤（2）...
【技术特征摘要】
1.一种增强型环保绝缘材料的制备方法，其特征在于：所述制备方法包括如下步骤：（1）按重量份配比准确称取各原料备用：HRB-6树脂80-120份、无碱玻璃纤维丝20-40份、聚丙烯纤维8-12份、增溶剂4-6份、纳米多孔二氧化硅16-24份、二甲基硅油5-15份和抗氧剂6-10份；（2）将HRB-6树脂、增溶剂、纳米多孔二氧化硅和抗氧剂依次加入密炼机中，以100转/min的转速搅...
【专利技术属性】
技术研发人员：唐正华，
申请(专利权)人：如皋市乐恒化工有限公司，
类型：发明
国别省市：江苏,32