The invention relates to an enhanced environmental protection and insulation materials, the enhanced environmental protection insulation material is composed of the following components in part by weight: 6 HRB 80 resin 120, alkali free glass fiber wire 20 40 and 8 polypropylene fiber 12 copies, 6 copies, 4 solubilizer nano porous silica 16 24 copies, two copies and 15 methyl silicone oil 5 antioxidant 6 10. The present invention has the advantages of high mechanical strength, good heat resistance and good breakdown resistance, and is an environmentally friendly insulating material with excellent comprehensive performance.
【技术实现步骤摘要】
一种增强型环保绝缘材料
本专利技术涉及绝缘材料
,特别涉及一种增强型环保绝缘材料。
技术介绍
聚酯由于其优异的成型加工性、电绝缘性和耐热性能被广泛应用于电子、电器和家电等行业。近年来,随着社会对环境问题的高度关注,聚酯中的环境友好型聚对苯二甲酸丁二醇酯(PBT)被广泛用于电气绝缘材料领域。电气领域通常指高温、高压环境,而普通的PBT材料因机械强度、耐热性和介电性能欠佳,在上述环境中易发生击穿破坏。
技术实现思路
本专利技术要解决的技术问题是提供一种能够满足高温、高压环境使用要求的增强型环保绝缘材料。为解决上述技术问题,本专利技术的技术方案为:一种增强型环保绝缘材料,其创新点在于:所述增强型环保绝缘材料是由以下重量份的组分组成:HRB-6树脂80-120份、无碱玻璃纤维丝20-40份、聚丙烯纤维8-12份、增溶剂4-6份、纳米多孔二氧化硅16-24份、二甲基硅油5-15份和抗氧剂6-10份。进一步地,所述增强型环保绝缘材料是由以下重量份的组分组成:HRB-6树脂90-110份、无碱玻璃纤维丝25-35份、聚丙烯纤维9-11份、增溶剂4.5-5.5份、纳米多孔二氧化硅18-22份、二甲基硅油8-12份和抗氧剂7-9份。进一步地,所述增强型环保绝缘材料是由以下重量份的组分组成:HRB-6树脂100份、无碱玻璃纤维丝30份、聚丙烯纤维10份、增溶剂5份、纳米多孔二氧化硅20份、二甲基硅油10份和抗氧剂8份。本专利技术的优点在于:本专利技术增强型环保绝缘材料,力学强度高、耐热性好,具有良好的耐击穿性能,是一种综合性能优异的环保绝缘材料。具体实施方式下面的实施例可以 ...
【技术保护点】
一种增强型环保绝缘材料,其特征在于:所述增强型环保绝缘材料是由以下重量份的组分组成:HRB‑6树脂80‑120份、无碱玻璃纤维丝20‑40份、聚丙烯纤维8‑12份、增溶剂4‑6份、纳米多孔二氧化硅16‑24份、二甲基硅油5‑15份和抗氧剂6‑10份。
【技术特征摘要】
1.一种增强型环保绝缘材料,其特征在于:所述增强型环保绝缘材料是由以下重量份的组分组成:HRB-6树脂80-120份、无碱玻璃纤维丝20-40份、聚丙烯纤维8-12份、增溶剂4-6份、纳米多孔二氧化硅16-24份、二甲基硅油5-15份和抗氧剂6-10份。2.根据权利要求1所述的增强型环保绝缘材料,其特征在于:所述增强型环保绝缘材料是由以下重量份的组分组成:HRB-6树脂90-11...
【专利技术属性】
技术研发人员:唐正华,
申请(专利权)人:如皋市乐恒化工有限公司,
类型:发明
国别省市:江苏,32