The invention discloses a method for grinding surface of the flywheel, which comprises the following steps: (1): grinding deburring brush grinding burr surface of the flywheel, the flywheel with wire brush grinding burrs on the inner wall of the cavity: (2) coarse grinding: the flywheel placed to remove the surface oxide layer in grinding grinder, grinding when the cooling water is used for flushing the entire surface of the flywheel; (3) fine grinding: the flywheel dry after rough grinding, using 400 600# dry sanding paper on the surface of the flywheel grinding ball; grinding head brush cavity wall. The deburring process of the flywheel surface is eliminated by the deburring step, which is convenient for the subsequent operation, and then the grinding wheel surface is smooth and smooth by the steps of coarse grinding and fine grinding, and the whole grinding process is safe and can not cause damage to the operator.
【技术实现步骤摘要】
一种飞轮表面的打磨方法
本专利技术属于飞轮处理
，尤其是涉及一种飞轮表面的打磨方法。
技术介绍
飞轮是安装在机器回转轴上的具有较大转动惯量的轮状蓄能器。当机器转速增高时，飞轮的动能增加，把能量贮蓄起来；当机器转速降低时，飞轮动能减少，把能量释放出来。然而目前的飞轮打磨工艺都依靠机械打磨，打磨时操作人员必须时刻集中精神，整个打磨过程危险性高，另外打磨后的飞轮表面光滑度和平整度较低，影响了飞轮的工作性能。
技术实现思路
本专利技术为了克服现有技术的不足，提供一种操作安全，工件表面光滑、平整的飞轮表面的打磨方法。为了实现上述目的，本专利技术采用以下技术方案：一种飞轮表面的打磨方法，包括如下步骤：（1）去毛刺：用研磨刷磨去飞轮表面的毛刺，用铁丝刷磨去飞轮孔洞内壁上的毛刺；（2）粗磨：将飞轮放置在砂轮机上打磨去除表面氧化层，打磨的时候用冷却水冲洗整个飞轮表面；（3）细磨：将经粗磨后的飞轮擦干，使用400-600#的干磨砂纸对飞轮表面进行打磨；用球头刷打磨孔洞内壁；用研磨刷清除飞轮表面的毛刺，有利于后续打磨操作的进行，飞轮放置在砂轮机上进行粗磨，能快速、有效的打磨掉飞轮表面...
【技术保护点】
一种飞轮表面的打磨方法，其特征在于：包括如下步骤：（1）去毛刺：用研磨刷磨去飞轮表面的毛刺，用铁丝刷磨去飞轮孔洞内壁上的毛刺；（2）粗磨：将飞轮放置在砂轮机上打磨去除表面氧化层，打磨的时候用冷却水冲洗整个飞轮表面；（3）细磨：将经粗磨后的飞轮擦干，使用400‑600#的干磨砂纸对飞轮表面进行打磨；用球头刷打磨孔洞内壁。
【技术特征摘要】
1.一种飞轮表面的打磨方法，其特征在于：包括如下步骤：（1）去毛刺：用研磨刷磨去飞轮表面的毛刺，用铁丝刷磨去飞轮孔洞内壁上的毛刺；（2）粗磨：将飞轮放置在砂轮机上打磨去除表面氧化层，打磨的时候用冷却水冲洗整个飞轮表面；（3）细磨：将经粗磨后的飞轮擦干，使用400-600#的干磨砂纸对飞轮表面进行打磨；用球头刷打磨孔洞内壁。2.根据权利要求1所述的飞轮表面的打磨方法，其特征在于：在...