The invention discloses a process for the preparation of magnetic sol gel glass beads, the invention by using TEOS as silicon source and tetrabutyl titanate as titanium source, adding ferric chloride alcohol solution mixed sols doped with iron, dispersed drops to certain temperature of paraffin wax, sol dispersion under surface tension and become a good round degree of the SiO2 TiO2 glass bead sphere; on the other hand can control the amount of alcohol solution by adding ferric chloride, ensure the glass bead has good refractive index at the same time, give the glass bead a certain magnetism, can be treated by magnetic field and beads, the preparation product has the performance of magnetic.
【技术实现步骤摘要】
一种溶胶-凝胶法制备磁性反光玻璃微珠的工艺方法
本专利技术涉及反光材料
，具体涉及一种磁性反光玻璃微珠的制造工艺方法。
技术介绍
玻璃微珠的制备方法中，喷吹法生产玻璃微珠工艺简单、成珠效率高、成本低，其缺点是微珠圆整度较差，有时容易出现“小尾巴”、“拉丝棉”等缺陷，需通过调节火焰温度与气流来解决此类缺陷，但其光学质量较好；隔离剂法成珠率高，产品圆整度好，可生产多种规格的玻璃微珠，其缺点是所生产的玻璃微珠表面粘有石墨粉，较难洗涤干净，易产生失透的玻璃微珠。溶胶-凝胶法是使用液体或易混合液体的混合物作为反应物，由于原料均匀混合在分子级的低粘度液体中并发生络合反应，制备高纯度玻璃和高均质度的多组分玻璃、玻璃陶瓷。使用溶胶-凝胶法可以在不改变组成的情形下，靠聚合物网络通过分子结构改型，即控制水解、凝聚等反应动力学以改变凝胶的聚合物结构而得到微观结构和性质不同的氧化物玻璃。另外由于胶体本身为网络体，玻璃或玻璃陶瓷的烧结温度大大降低，很大程度上降低了生产成本。
技术实现思路
本专利技术提供了一种磁性反光玻璃微珠的制造工艺方法，在保证玻璃微珠具有良好折射率的同时，赋予玻璃微珠...
【技术保护点】
一种溶胶‑凝胶法制备磁性反光玻璃微珠的工艺方法，其特征在于，包括以下具体步骤：（1）杂铁钛溶胶的制备：将20‑40重量份钛酸四丁酯缓慢滴加到240‑480份无水乙醇/水混合液中，加入0.03‑0.1份乙酰丙酮作为水解抑制剂，调节pH 值为3.2‑4.0，之后加入10‑20份20‑40%FeCl3醇溶液，混合均匀；（2）制备硅溶胶：在剧烈搅拌条件下，将60‑80份正硅酸乙酯加入250‑400份去离子水中，同时使用0.5M盐酸溶液调节溶胶体系pH值在2.8‑3.4；（3）水解：待步骤（2）硅溶胶已成透明状且内部无气泡产生时，缓慢滴入步骤（1）均匀的掺杂铁钛溶胶，超声分散15‑3...
【技术特征摘要】
1.一种溶胶-凝胶法制备磁性反光玻璃微珠的工艺方法，其特征在于，包括以下具体步骤：（1）杂铁钛溶胶的制备：将20-40重量份钛酸四丁酯缓慢滴加到240-480份无水乙醇/水混合液中，加入0.03-0.1份乙酰丙酮作为水解抑制剂，调节pH值为3.2-4.0，之后加入10-20份20-40%FeCl3醇溶液，混合均匀；（2）制备硅溶胶：在剧烈搅拌条件下，将60-80份正硅酸乙酯加入250-400份去离子水中，同时使用0.5M盐酸溶液调节溶胶体系pH值在2.8-3.4；（3）水解：待步骤（2）硅溶胶已成透明状且内部无气泡产生时，缓慢滴入步骤（1）均匀的掺杂铁钛溶胶，超声分散15-30分钟，在搅拌和0℃温度下，向混合溶胶中滴加70-140份蒸馏水，搅拌1.5-3小时；（4）然后边搅拌边将步骤（3）混合溶胶缓缓滴入到液体石蜡中，并置于40-50℃恒温水浴槽中，搅拌至...
【专利技术属性】
技术研发人员：范春平，
申请(专利权)人：合肥鼎亮光学科技有限公司，
类型：发明
国别省市：安徽,34