The invention discloses a process for preparing activated carbon vacuum chemical activation method, which comprises the following steps: (1) clean raw material after drying with ZnCl2 solution impregnated 24h; (2) drying, placed in the reactor; (3) sequentially connected water condenser, cold trap, vacuum pump, vacuum pump adjustment the 0.1~0.2 atmospheric pressure; (4) the startup of the reactor, the initial temperature of 25 degrees Celsius, heating time 50 55 minutes, the final temperature of 500 degrees Celsius 600; (5) stop heating, temperature drop to 200 degrees Celsius, turn off the vacuum pump, the solid product of mobile phone in the reactor. The beneficial effects of the invention are: using zinc chloride as activator, in vacuum pyrolysis of activated carbon, the process of cleaning, introduced and vacuum conditions reduce the activation temperature, thereby reducing the energy consumption, but also makes the vacuum conditions of bio oil collection more convenient.
【技术实现步骤摘要】
一种真空化学活化法制备活性炭的工艺
本专利技术涉及吸附剂制备
，具体为一种真空化学活化法制备活性炭的工艺。
技术介绍
活性炭作为一种重要的微孔吸附剂，具有丰富的空姐后和极大的比表面积，表面含有多种含氧官能团，催化活性和化学稳定性好，易反复使用，在工业、农业、国防、科技及生活中得到广泛应用，成为一种国民经济不可缺少的重要吸附剂。现有的活性炭制备都是在常压下进行的，能耗较高。
技术实现思路
本专利技术的目的在于提供一种真空化学活化法制备活性炭的工艺，以解决上述
技术介绍
中提出的问题。为实现上述目的，本专利技术提供如下技术方案：一种真空化学活化法制备活性炭的工艺，包括如下步骤：（1）原料经清洗干净干燥后用ZnCl2溶液浸渍24h；（2）烘干，置于反应器中；（3）顺序连接好水冷凝器、冷阱、真空泵，调节真空泵使其达到0.1~0.2个大气压；（4）启动反应器，设定初始温度25摄氏度，升温时间50-55分钟，终温500-600摄氏度；（5）停止加热，温度下降到200摄氏度时，关掉真空泵，手机反应器中的固体产物。优选的，所述原料为杉木屑。优选的，所述ZnCl2与杉木屑的质量比为1...
【技术保护点】
一种真空化学活化法制备活性炭的工艺，其特征在于：包括如下步骤：（1）原料经清洗干净干燥后用ZnCl2溶液浸渍24h；（2）烘干，置于反应器中；（3）顺序连接好水冷凝器、冷阱、真空泵，调节真空泵使其达到0.1~0.2个大气压；（4）启动反应器，设定初始温度25摄氏度，升温时间50‑55分钟，终温500‑600摄氏度；（5）停止加热，温度下降到200摄氏度时，关掉真空泵，手机反应器中的固体产物。
【技术特征摘要】
1.一种真空化学活化法制备活性炭的工艺，其特征在于：包括如下步骤：（1）原料经清洗干净干燥后用ZnCl2溶液浸渍24h；（2）烘干，置于反应器中；（3）顺序连接好水冷凝器、冷阱、真空泵，调节真空泵使其达到0.1~0.2个大气压；（4）启动反应器，设定初始温度25摄氏度，升温时间50-55分钟，终温500-600摄氏度；（5）停止加热，温度下降到2...