一种聚三氟氯乙烯超长棒立式模压成型模具制造技术

一种聚三氟氯乙烯超长棒立式模压成型模具，其特征在于：立式模压成型模具包括上下加压杆、上下料腔、上下滑块、塑腔、锁紧螺栓、加热器、上下压环；上下滑块设置在立式模压成型模具中心，对称布置在塑腔的两端的料孔的上下端口，且通过控制上下滑块与聚三氟氯乙烯棒材模压最小高度，保证超长料的高度。

A super long rod vertical die for forming three poly vinyl chloride

A poly three vinyl fluoride long rod vertical molding mould, which is characterized in that the vertical molding mould includes upper and lower pressure rod, upper and lower material cavity, upper and lower slide, plastic cavity, a locking bolt, a heater, a lower pressing ring; upper and lower vertical slider arranged in the molding mold, symmetry layout holes at both ends of the plastic cavity on the port, and through the control on the slider and the poly three vinyl fluoride molded bar minimum height, the height of material guarantee long.

【技术实现步骤摘要】
一种聚三氟氯乙烯超长棒立式模压成型模具
本技术涉及到一种材料的辅助作业装置，具体涉及一种聚三氟氯乙烯超长棒立式模压成型模具，该种立式模压成型模具，主要用于制作直径在50mm左右，长度超过200mm以上的超长聚三氟氯乙烯园棒制品，属于工装模具

技术介绍
聚三氟氯乙烯（PCTFE）是可熔融氟塑料系列材料中，机械强度佳、抗低温性能（-200℃环境中不发脆）优的品种之一，已广泛用于液氧、液氮及其他低温状态下强腐蚀性介质的密封或应用于航空、航天等高科技尖端
的特殊密封。目前，工业发达的西方国家，利用材料合成技术的优势，已突破了直径Φ15以内棒材连续挤出成型与直径Φ60*300棒材卧式模压成型技术，但成型技术对外十分保密，而我国材料合成技术处于提质阶段，原料依赖进口。因此，开展成型工艺研究具有十分重要意义。通过专利检索没发现有与本专利技术相同技术的专利文献报道，与本专利技术有一定关系的专利主要有以下几个：1、专利号为CN201510297605.6，名称为“改性聚三氟氯乙烯及其模压工艺”的专利技术专利，该专利公开了一种改性聚三氟氯乙烯及其模压工艺，一种改性聚三氟氯乙烯，改性聚三氟本文档来自技高网...

【技术保护点】
一种聚三氟氯乙烯超长棒立式模压成型模具，其特征在于：立式模压成型模具包括上下加压杆、上下料腔、上下滑块、塑腔、锁紧螺栓、加热器、上下压环；上下滑块设置在立式模压成型模具中心，对称布置在塑腔的两端的料孔的上下端口，且通过控制上下滑块与聚三氟氯乙烯棒材模压最小高度，保证超长料的高度。

【技术特征摘要】
1.一种聚三氟氯乙烯超长棒立式模压成型模具，其特征在于：立式模压成型模具包括上下加压杆、上下料腔、上下滑块、塑腔、锁紧螺栓、加热器、上下压环；上下滑块设置在立式模压成型模具中心，对称布置在塑腔的两端的料孔的上下端口，且通过控制上下滑块与聚三氟氯乙烯棒材模压最小高度，保证超长料的高度。2.如权利要求1所述的聚三氟氯乙烯超长棒立式模压成型模具，其特征在于：所述的通过控制上下滑块与聚三氟氯乙烯棒材模压最小高度是在上下滑块厚度为50时，聚三氟氯乙烯棒材模压最小高度H为：H=2倍滑块厚度+（制品端面积×制品高度×产品密度）/（制品端面积×材料表面密度）。3.如权利要求2所述的聚三氟氯乙烯超长棒立式模压成型模具，其特征在于：所述的聚三氟氯乙烯棒材模压最小高度H限定在1200-...