一种石墨片的制备方法技术
Preparation method of graphite flake
A graphite sheet preparation method comprises the following steps: selecting graphite powder slurry, the slurry storage in graphite powder coating equipment; graphite powder coating on carbon fiber substrate, and then sent to the calender by calendering, the Graphite Slurry and carbon fiber substrate are combined into a whole, and then rolling the formation of the web material; graphite powder slurry and carbon fiber substrate combined sent to graphitization of the graphite furnace; graphitization after cooling, and then spread to the calender roll again in the rolling process, the membrane surface, and finally the rolling operation, to obtain graphene sheet. The graphite flakes prepared by the invention have high thermal conductivity, high purity, strong tensile strength and tear resistance, and high bending strength.
【技术实现步骤摘要】
一种石墨片的制备方法
本专利技术属于石墨
，具体地说是一种石墨片的制备方法。
技术介绍
目前，各类型的电子终端，如笔记本电脑、平板电脑、智能手机等，这些设备的功能越来越强大，运算速度越来越快，越来越轻薄，从而使得散热成为一个难以回避的问题，由于产品整体上来越来轻薄，因此其产生的热量或者发热点也越来越集中。石墨片作为一种散热性能较佳的散热产品，已经得到越来越广泛用应用，尤其是石墨片本身的厚度较小，对于智能手机、平板电脑等需要轻薄型的电子设备来说，更具有优越的性能。传统的石墨片通常是由石墨粉经过压延机压制成型，然后经收卷操作形成一卷一卷的石墨片。此方法制备得到的石墨片，纯度较低，导热系数较低，并且抗拉伸、抗弯曲强度和抗撕裂性能都较小，在很多场合都难难以满足使用条件。
技术实现思路
本专利技术要解决的技术问题是一种石墨片的制备方法，制备得到的石墨片，导热系数高，纯度高，具有较强的抗拉伸强度和抗撕裂性，同时抗弯曲强度高。为了解决上述技术问题，本专利技术采取以下技术方案：一种石墨片的制备方法，包括以下步骤：选取石墨粉浆料，将该石墨粉浆料储存在涂覆设备上；将石墨粉浆料涂覆在...
【技术保护点】
一种石墨片的制备方法，包括以下步骤：选取石墨粉浆料，将该石墨粉浆料储存在涂覆设备上；将石墨粉浆料涂覆在碳纤维基材上，然后送到压延机进行辊压成型，使石墨粉浆料与碳纤维基材结合成一体，再进行收卷形成卷材；将石墨粉浆料与碳纤维基材结合成一体的卷材送到石墨化炉中进行石墨化处理；石墨化处理完成后冷却，然后卷材伸展开送到压延机中再次辊压处理，使卷材表面平整，最后再进行收卷操作，得到成品石墨片卷材。
【技术特征摘要】
1.一种石墨片的制备方法，包括以下步骤：选取石墨粉浆料，将该石墨粉浆料储存在涂覆设备上；将石墨粉浆料涂覆在碳纤维基材上，然后送到压延机进行辊压成型，使石墨粉浆料与碳纤维基材结合成一体，再进行收卷形成卷材；将石墨粉浆料与碳纤维基材结合成一体的卷材送到石墨化炉中进行石墨化处理；石墨化处理完成后冷却，然后卷材伸展开送到压延机中再次辊压处理，使卷材表面平整，最后再进行收卷操作，得到成品石墨片卷材。2.根据权利要求1所述的石墨片的制备方法，其特征在于，所述石墨粉浆...
【专利技术属性】
技术研发人员：任泽明，王号，张建辉，
申请(专利权)人：广东思泉新材料股份有限公司，
类型：发明
国别省市：广东,44