涂覆铁基非晶金属涂层的火电厂引风机叶轮制造技术
The coating of Fe based amorphous metal coating of the thermal power plant fan impeller
The invention provides a coating of Fe based amorphous metal coating of the thermal power plant fan impeller, the technical scheme is as follows: using emery sand or equivalent hardness of water cooling wall for sand blasting surface texturing, removing the oxide layer and the attachment, roughness of Sa12.5 micron. The amorphous alloy was sprayed by supersonic arc spraying. The coating thickness was 0.4mm. The invention has the advantages of reasonable and practical design, time saving and labor saving, and the service life of the impeller is increased by more than 3 times, which is suitable for popularization and use.
【技术实现步骤摘要】
涂覆铁基非晶金属涂层的火电厂引风机叶轮
本专利技术涉及设备涂层
，尤其是涂覆铁基非晶金属涂层的火电厂引风机叶轮。
技术介绍
引风机叶轮是火电厂锅炉排放烟尘的主要设备，烟尘中的颗粒物和含有腐蚀性的水气在强风推送下冲刷叶轮表面。在腐蚀和磨损共同作用下，叶轮的寿命一般较短，有的寿命仅有三个月。现有叶轮一般采用碳钢、锰钢、硬质合金等材料或者叶轮外部涂覆合金涂层、采用玻璃钢等材料进行防护，虽然一定程度上延长了叶轮寿命，但为期太短，不能从根本上解决叶轮的使用寿命问题。
技术实现思路
本专利技术经多年实践提供最先进的技术，把美国LMC公司的专有铁基非晶合金涂覆到叶轮表面上来，解决引风机叶轮使用寿命短的问题。非晶合金又称为液态金属，是指材料在固态条件下保留了金属在液态状况下原子的三维空间无序排列，也就是金属没有了固有的晶界，由于晶界的消失，和传统合金比较，非晶合金的耐腐蚀性、硬度和韧性大大增强，美国LiquidMetalCoatingLLC公司(简称LMC)是该材料在全球该领域的领军企业。通过热喷涂技术，把非晶合金涂覆在叶轮表面，从而大大提高其使用寿命。本专利技术的目的是通过以下技术方案实现的：采用金刚砂或同等硬度砂石对水冷壁表面进行喷砂毛化处理，去除氧化层和附着物，粗糙度达到Sa12.5微米。采用超音速电弧喷涂技术喷涂非晶合金材料，喷涂厚度为0.4mm。采用封孔剂进行封孔处理。叶轮直径1.8m，采用Q235钢，工作转速980r/min,风量154000m3/h,煤粉含硫量18000mg/m3,煤粉含水量25％。本专利技术的有益效果：本专利技术设计合理实用，省时省力，提...
【技术保护点】
涂覆铁基非晶金属涂层的火电厂引风机叶轮，其特征在于：采用金刚砂或同等硬度砂石对水冷壁表面进行喷砂毛化处理，去除氧化层和附着物，粗糙度达到Sa12.5微米。
【技术特征摘要】
1.涂覆铁基非晶金属涂层的火电厂引风机叶轮，其特征在于：采用金刚砂或同等硬度砂石对水冷壁表面进行喷砂毛化处理，去除氧化层和附着物，粗糙度达到Sa12.5微米。2.根据权利要求1所述的涂覆铁基非晶金属涂层的火电厂引风机叶轮，其特征在于：采用超音速电弧喷涂技术喷涂非晶合金材料，喷涂厚度为0.4mm。3.根据权利...