The invention relates to a method for four carbon olefin gasoline components production of ethylene or propylene, which mainly solves four carbon olefin oligomerization gasoline component and lower liquid ethylene propylene low content of the problem in the prior art. The invention adopts four carbon olefin gasoline components production of ethylene or propylene, which comprises the following steps: in the presence of ZSM 35 catalyst, four carbon olefin gasoline components and reaction of ethylene or propylene; the molar ratio of ZSM 35 catalyst SiO2/Al2O3 was 10 ~ 19, the reaction temperature is 360 to 390 DEG C, reaction pressure is 0 ~ 0.1MPa scheme can solve this problem well, can be used for four carbon olefin gasoline components production of ethylene or propylene in industrial production.
【技术实现步骤摘要】
碳四烯烃制汽油组分联产乙烯或丙烯的方法
本专利技术涉及碳四烯烃制汽油组分联产乙烯或丙烯的方法。
技术介绍
C4低碳烯烃和含有C4低碳烯烃的混合烃类是石化和炼油行业的副产物，产自乙烯工程、炼油厂和天然气净化等过程。混合碳四烯烃中除少数组分被抽提用作化工原料外，很大部分都用作廉价燃料，主要原因是燃料价格较高。随着我国西部大开发战略和西气东输工程的顺利实施，以及从煤出发合成二甲醚技术的大规模使用，混合碳四烯烃终将被管道天然气等更为廉价的燃料逐渐挤出民用市场。通过催化工艺将这些混合碳四烯烃转化为汽油组份，不仅可为汽油的生产开辟新原料来源，且可优化利用轻烃资源，提高石化企业经济效益。另一方面，丁基醚(MTBE)、乙基叔丁基醚(ETBE)在新配方汽油和含氧汽油中显示出较高的辛烷值、低蒸汽压以及在汽油馏分烃类中的良好溶解性而使其成为优良的汽油添加组分，需求量在全球迅速增加，致使许多醚化装置都进行了扩产。在生产MTBE的醚化装置的出口物料中，分出甲醇和醚之后，正构烯烃占到40-100重量％，装置的扩产将产生大量醚后的正丁烯资源，目前主要作为液化气烧掉，急需寻找新的用途。将含烯烃的...
【技术保护点】
碳四烯烃制汽油组分联产乙烯或丙烯的方法，包括以下步骤：在ZSM‑35催化剂存在下，碳四烯烃进行反应生成汽油组分联产乙烯或丙烯；ZSM‑35催化剂的SiO2/Al2O3的摩尔比为10～19，反应温度为360～390℃，反应压力为0～0.1MPa。
【技术特征摘要】
1.碳四烯烃制汽油组分联产乙烯或丙烯的方法，包括以下步骤：在ZSM-35催化剂存在下，碳四烯烃进行反应生成汽油组分联产乙烯或丙烯；ZSM-35催化剂的SiO2/Al2O3的摩尔比为10～19，反应温度为360～390℃，反应压力为0～0.1MPa。2.根据权利要求1所述的方法，其特征是ZSM-35催化剂的SiO2/Al2O3摩尔比为15～19。3.根据权利要求1所述的方法，其特征是反应温度为370～380℃。4.根据权利要求1所述的方法，其特征是所述的四烯烃为反丁烯、顺丁烯、丁烯-1、异丁烯中的一种或多种。5.权利要求1中所述催化剂的制备方法，包括以下步骤：a)将SiO2/Al2O3摩尔比为10～19的ZSM-35分子筛在温度为30～90℃、碱浓度为1.0M以下的条件下碱处理0.1～40小时，...
【专利技术属性】
技术研发人员：李云龙，吕建刚，金照生，金萍，周海春，葛怡丽，李晓明，刘波，
申请(专利权)人：中国石油化工股份有限公司，中国石油化工股份有限公司上海石油化工研究院，
类型：发明
国别省市：北京,11
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。