The invention relates to a HDPE composite material and preparation method thereof, wherein the HDPE composite material by weight consists of the following components: 80 for HDPE 100; 10 for PBT 16; 0.1 for DCP 0.3; nano TiO2 0.1 0.3; antioxidant 0.1 0.5. The effect of nano TiO2 is two: (1) the addition of TiO2 plays a nucleating agent in the HDPE matrix, which induces the crystallization of HDPE and improves the physical properties of HDPE composites. Join the TiO2, improve the compatibility of HDPE and PBT interface to a certain extent, the bond between the two is firm; two peroxide cumene as initiator can make HDPE a free radical, radical ions and HDPE and crosslinked PBT, which further form a three-dimensional network structure to improve the compatibility of HDPE and PBT interface, but also conducive to improve the performance of HDPE composite material.
【技术实现步骤摘要】
一种HDPE复合材料及其制备方法
本专利技术属于高分子材料
，特别是指一种HDPE复合材料及其制备方法。
技术介绍
高密度聚乙烯(HDPE)是一种广泛应用的高分子树脂，它具有良好的耐疲劳性，较好的耐热性，优良的尺寸稳定性等优点。但是它的物理性能一般，在一些家电、汽车的应用领域，对物理性能有很高的要求，普通HDPE不能满足这种要求，这就大大限制了HDPE复合材料的应用范围。
技术实现思路
本专利技术的目的是提供一种HDPE复合材料及其制备方法，以解决现技术普通HDPE材料的应用受到限制的问题。本申请创新的利用PBT改性HDPE，并用过氧化二异丙苯(DCP)和纳米TiO2来改善HDPE和PBT的相容性，优化现有HDPE复合材料的力学性能，这对于扩展HDPE复合材料的应用具有非常重要的现实意义。本专利技术是通过以下技术方案实现的：一种HDPE复合材料，按重量份由以下组分组成：所述纳米TiO2为20-30nm。所述纳米TiO2是经过硅烷偶联剂KH550处理后的纳米TiO2。所述抗氧剂为三(2,4-二叔丁基)亚磷酸苯酯、四[β-(3，5-二叔丁基-4-羟基苯基)丙酸]季戊...
【技术保护点】
一种HDPE复合材料，其特征在于，按重量份由以下组分组成：
【技术特征摘要】
1.一种HDPE复合材料，其特征在于，按重量份由以下组分组成：2.根据权利要求1所述的HDPE复合材料，其特征在于，所述纳米TiO2为20-30nm。3.根据权利要求1所述的HDPE复合材料，其特征在于，所述纳米TiO2是经过硅烷偶联剂KH550处理后的纳米TiO2。4.根据权利要求1所述的HDPE复合材料，其特征在于，所述抗氧剂为三(2,4-二叔丁基)亚磷酸苯酯、四[β-(3，5-二叔丁基-4-羟基苯基)丙酸]季戊四醇酯或1，3，5-三甲基-2，4，6-(3，5-二叔丁基-4-羟基苯甲基)苯中的一种或几种的混合。5.上述权利要求1至4中任一项HDPE复合材料的制备方法，其特征在于，包括以下步骤：(1)称取80份-...
【专利技术属性】
技术研发人员：刘凯，徐志海，孙启林，
申请(专利权)人：安徽江淮汽车集团股份有限公司，
类型：发明
国别省市：安徽,34