A method for preparing ceramic composite emulsion pump plunger, the first six alumina, boron nitride, Magnesium Oxide, calcium oxide, Diopside is fully mixed with the mullite whisker after mixing granulation powder in the mold forming the medium pressure, sintered compact alumina ceramic plunger blank, finally through grinding into ceramic plunger with precision size and precision; compared with the prior art, the ceramic plunger material of the invention can improve the toughness of ceramic plunger effectively, reduce the friction coefficient of the plunger, improve grinding and finished product ratio of material and improve the service life of the ceramic plunger.
【技术实现步骤摘要】
一种用于乳化泵柱塞的陶瓷复合材料的制备方法
本专利技术涉及陶瓷复合材料制备领域，特别涉及一种用于乳化泵柱塞的陶瓷复合材料的制备方法。
技术介绍
乳化液泵站是综采工作面的关键设备之一，其正常运行直接影响高产高效工作面的生产效益。由于乳化液泵的工作周期较长，故对其关键件陶瓷柱塞的质量要求相当严格。从耐磨性进行比较，氧化锆陶瓷是增韧氧化铝陶瓷的2倍，增韧氧化铝陶瓷是氧化铝陶瓷的4倍以上；从断裂韧性进行比较，氧化锆陶瓷是增韧氧化铝的陶瓷的2-3倍，增韧氧化铝陶瓷是氧化铝陶瓷的2倍左右。氧化锆陶瓷性能最适合煤矿的使用条件，但从经济角度上考虑,氧化锆陶瓷价格昂贵、性价比低，氧化铝陶瓷价格便宜但耐磨性和韧性不够。因此乳化液泵柱塞材料选择增韧氧化铝陶瓷最为合理，并且柱塞在运动过程中可能产生局部瞬时的热量，增韧氧化铝陶瓷比氧化锆在高温下更加稳定。晶须是具有一定长径比(直径0.1-1.8um，长35-150um)，且缺陷少的陶瓷单晶。具有很高的强度，是一种非常好的陶瓷基复合材料的增韧增强体；纤维长度较陶瓷晶须长数倍，也是一种很好的陶瓷增韧体，同时两者可复合实用。用SiC、Si3N4等...
【技术保护点】
一种用于乳化泵柱塞的陶瓷复合材料的制备方法，其特征在于，包括以下步骤：步骤一；成形粉料的调制：将氧化铝粉与六方氮化硼、氧化镁、氧化钙、透辉石充分混合后再与莫来石晶须进行充分混合，得到的粉体进行造粒；所述的造粒粉体包括以下组分及重量份数：氧化铝65‑90，六方氮化硼2‑6，氧化镁1‑3，氧化钙1‑5，透辉石1‑5，莫来石晶须5‑20；步骤二；等静压成型；将步骤一中得到的混合物颗粒置于模具中冷等静压成形，成形压力200‑500MPa，保压时间1‑10min得坯体；步骤三；高温烧结；将得到的坯体进行高温烧结成致密化铝复合材料坯体，高温烧结温度为1500‑1600℃；步骤四；磨削加...
【技术特征摘要】
1.一种用于乳化泵柱塞的陶瓷复合材料的制备方法，其特征在于，包括以下步骤：步骤一；成形粉料的调制：将氧化铝粉与六方氮化硼、氧化镁、氧化钙、透辉石充分混合后再与莫来石晶须进行充分混合，得到的粉体进行造粒；所述的造粒粉体包括以下组分及重量份数：氧化铝65-90，六方氮化硼2-6，氧化镁1-3，氧化钙1-5，透辉石1-5，...
【专利技术属性】
技术研发人员：王旭东，杨建锋，王子敬，张亚明，王波，李春芳，
申请(专利权)人：府谷县旭丽机电技术有限公司，西安交通大学，
类型：发明