The invention relates to an antistatic ceramic fired by roller kiln with a large amount of red mud as raw material and a preparation method thereof, which belongs to the field of ceramic preparation technology. The anti-static ceramic is composed of the following raw materials: the mass percentage of red mud from 55 to 75%, kaolin 5%, cooked pyrojewel 10%, 3 ~ 12% high temperature refractory clay, feldspar 7 ~ 18%; the preparation method is the proportion of raw material mixture, then in accordance with the quality of water and raw material ratio the proportion of 35: 65 water mixing, grinding, drying and grinding powder obtained by balling machine, or hand made ceramic powder, 200MPa molding, drying 1H at 150 DEG C in roller kiln, by 1150 to 1160 DEG C for firing, anti-static ceramic. The invention adopts the red mud amount of raw materials, to anti-static index by adjusting the amount of red mud to facilitate the regulation of anti-static ceramic, with small deformation, non foaming anti-static ceramic roller kiln firing time, high production efficiency, is conducive to large-scale industrial production.
【技术实现步骤摘要】
以大掺量赤泥为原料经辊道窑烧成的防静电陶瓷及其制备方法
本专利技术涉及一种以大掺量赤泥为原料经辊道窑烧成的防静电陶瓷及其制备方法，属于陶瓷制备
技术介绍
赤泥作为氧化铝行业的副产物，其排放量非常大，我国每年产生的赤泥废弃物达1000万吨，废弃物随意堆放会对大气、水和土壤等环境产生严重影响，因此，发展赤泥的循环利用技术迫在眉睫。赤泥的含铁量高，也含有高温下能够分解的碳酸钙，在将其作为陶瓷原料使用时，赤泥中的铁组分在高温烧成时易形成低熔点的液相，而碳酸盐分解产生的气体会在陶瓷坯体中带来孔隙、在釉料层中带来针孔缺陷，近年来，多是发展利用添加赤泥的方法来生产发泡陶瓷，如ZL201510283089.1公开了一种添加瓷砖废料并经辊道窑烧成发泡赤泥瓷砖的方法，通过调控原料配方，利用高温烧成过程中气体释放行为的控制来生产得到发泡赤泥瓷砖。在不发泡陶瓷的生产过程中，赤泥的添加量一直较低，ZL201210295391.5公开了利用添加15％赤泥原料来生产得到仿古砖，这是因为赤泥含量高给坯体带来高温下降低粘度的熔剂组分就多，高温烧成时陶瓷易变形、过烧，高温下液相出现过早，气...
【技术保护点】
一种以大掺量赤泥为原料经辊道窑烧成的防静电陶瓷，其特征在于：由以下质量百分数的原料制成：
【技术特征摘要】
1.一种以大掺量赤泥为原料经辊道窑烧成的防静电陶瓷，其特征在于：由以下质量百分数的原料制成：2.根据权利要求1所述的以大掺量赤泥为原料经辊道窑烧成的防静电陶瓷，其特征在于：熟焦宝石是将焦宝石在1300℃下煅烧2h后而制得。3.一种权利要求1或2所述的以大掺量赤泥为原料经辊道窑烧成的防静电陶瓷的制备方法，其特征在于：包括以下步骤...
【专利技术属性】
技术研发人员：姚奇恒，袁东峰，张辉，袁飞，
申请(专利权)人：淄博金狮王科技陶瓷集团有限公司，
类型：发明
国别省市：山东,37
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。