The invention discloses a method for producing building materials of high performance composite soil, with raw soil as base material, admixture of polypropylene fiber, silica fume, shell powder, lime, fly ash, cement, gravel, sand or gravel, zeolite powder. Admixture component quality percentage is 8%, 1.5 lime cement 5 16% and 0.1 polypropylene fiber 2%, 0.2 shell powder 1.5%, 4%, 0 silica fume fly ash 0 8%, 10%, 3 gravel and zeolite powder 1 3%, 2 6% sand. The composite soil building materials can be cured after molding and curing, and the curing time is about 28 days. Composite soil strength building materials produced using this method of production increased significantly, which can be applied to the construction of the building block, wall body, foundation cushion, foundation pit, can also be used in hydraulic engineering, railway, highway construction and municipal engineering, forestry and field and restoration of ancient buildings, there are resources to spoil the use.
【技术实现步骤摘要】
一种高性能复合土建材的制作方法
本专利技术属于再生资源综合利用领域，特别指一种高性能复合土环保建材的制作方法。
技术介绍
我国近年来随着开发建设的快速发展，产生了大量弃土难于处置，在一些大中城市产生弃土围城现象，污染环境，有些堆土还成为安全隐患。因此如何实现弃土的资源化利用成为我国城乡绿色发展、和谐发展需要迫切解决的问题。这些弃土，特别是各类土木工程、交通工程、水利工程等的基坑开挖产生的土方大部分都是生土。关于生土的利用，在我国有很长的历史，在陕西、山西、福建、广东等省现存的一些古建筑、古村落都有用生土建造的古墙、古屋。生土建筑近年来在国外也受到重视，由于生土建筑减少钢筋、水泥、能源的消耗，因而被看做绿色建筑的重要内容。但是生土建材也存在一些缺点，如抗拉强度和抗压性能较低，无侧限抗压强度小于1MPa，耐水能力较差，易产生较大变形等，这限制了生土建材的应用。本专利技术的目的是为提高生土建材的强度等性能指标，特别是利用生土弃土开发含有多种添加剂的高性能复合土，这种复合土可以广泛应用于建筑中的砌块、墙体、基础垫层、基坑支护，也可应用于水利工程，铁路、公路建设和市政工程，...
【技术保护点】
一种高性能复合土建材的制作方法，其技术特征为成分是以生土为基材，掺和料为聚丙烯纤维、硅粉、贝壳粉、石灰、粉煤灰、水泥、碎石或者卵石、沸石粉、砂。
【技术特征摘要】
1.一种高性能复合土建材的制作方法，其技术特征为成分是以生土为基材，掺和料为聚丙烯纤维、硅粉、贝壳粉、石灰、粉煤灰、水泥、碎石或者卵石、沸石粉、砂。2.根据权利要求1提出的一种高性能复合土建材的制作方法，其技术特征为掺和料组分质量百分比为石灰1.5-8％，水泥5-16％，聚丙烯纤维0.1-2％，贝壳粉0.2-1...
【专利技术属性】
技术研发人员：张强，张玉昌，
申请(专利权)人：深圳市瀚润达生态环境技术有限公司，
类型：发明
国别省市：广东,44
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。