一种高铁用接线鼻的制造方法技术
Manufacturing method of junction nose for high speed railway
Method of manufacturing wiring nose with a high iron, the terminal nose including copper layer, and the copper layer composite aluminum layer, in the manufacture of copper and aluminum, the first will be stacked together, and then subjected to friction stir welding of copper and aluminum can be combined together in copper or aluminum; friction welding the operation of mixing in multi friction stir welding, friction stir welding - welding path connected or overlapped, thereby forming copper or aluminum plate surface welding. The invention adopts the friction stir welding of composite, and the composite surface were subjected to friction stir welding, thus forming the welding surface between copper and aluminum composite, the strength is very high, timely connection nose bent 120 degrees will not produce welding tearing phenomenon of tilt.
【技术实现步骤摘要】
一种高铁用接线鼻的制造方法
本专利技术涉及一种高铁用接线鼻的制造方法。
技术介绍
高铁用接线鼻用于高铁线路的接线，该接线鼻包括铜层、与铜层复合的铝层，接线时铜部件与铜层对接，铝部件与铝层对接。在现有技术中，高铁用接线鼻的制造方法是采用爆炸焊的方法将铜板和铝板焊接在一起，其复合强度较低，接线鼻稍有弯折其铜板与铝板的焊接处就被撕裂。
技术实现思路
为了克服现有技术中高铁用接线鼻的制造方法的不足，本专利技术提供一种制造出的产品复合强度高的高铁用接线鼻的制造方法。本专利技术解决其技术问题的技术方案是：一种高铁用接线鼻的制造方法，该接线鼻包括铜层、与所述的铜层复合的铝层，在制造时，首先将铜板和铝板叠在一起，然后在铜板或铝板上施以搅拌摩擦焊从而将铜板和铝板复合在一起；在进行搅拌摩擦焊时进行多道搅拌摩擦焊操作，多道搅拌摩擦焊的焊接路径相接或重叠，从而使铜板或铝板上形成焊接面。进一步，搅拌摩擦焊操作完成后，将已复合完毕的铜板和铝板进行机械加工。进一步，在铜板和铝板中较薄的一块板上进行搅拌摩擦焊，在较薄的一块板上进行搅拌摩擦焊，其焊接难度较小、焊接效果也较好，当然也可以是在较厚的一块板...
【技术保护点】
一种高铁用接线鼻的制造方法，该接线鼻包括铜层、与所述的铜层复合的铝层，其特征在于：在制造时，首先将铜板和铝板叠在一起，然后在铜板或铝板上施以搅拌摩擦焊从而将铜板和铝板复合在一起；在进行搅拌摩擦焊时进行多道搅拌摩擦焊操作，多道搅拌摩擦焊的焊接路径相接或重叠，从而使铜板或铝板上形成焊接面。
【技术特征摘要】
1.一种高铁用接线鼻的制造方法，该接线鼻包括铜层、与所述的铜层复合的铝层，其特征在于：在制造时，首先将铜板和铝板叠在一起，然后在铜板或铝板上施以搅拌摩擦焊从而将铜板和铝板复合在一起；在进行搅拌摩擦焊时进行多道搅拌摩擦焊操作，多道搅拌摩擦焊的焊接路径相接或重叠，从而使铜板或铝板上形成焊接面。2.如权利要求1所述的高铁用接线鼻的制造方法，其特征在于：搅拌摩擦焊操作完成后，将已复合完毕的铜板和铝板进行机械加工。3.如权利要求1或2所述的高铁用接线鼻的制造方法，其...
【专利技术属性】
技术研发人员：章德均，刁海波，
申请(专利权)人：宁波金凤焊割机械制造有限公司，
类型：发明
国别省市：浙江,33