The invention provides a Fe based powder metallurgy friction material, which comprises the following raw materials in parts by weight: iron 55~72, 6~15 copper, graphite 4~10, silica powder 3~6, boron carbide powder 2~5 parts, silicon carbide 3~6, two molybdenum oxide powder 2~6 parts, two zirconia powder 1~ 4 copies. Precipitated barium sulfate powder 3~10 parts, chromium oxide powder 1~3, nickel powder 1~4 parts. The friction material provided by the invention improves the friction system, at the same time protect the dual parts, effectively improve the material bearing capacity, thermal stability, wear resistance, and good thermal conductivity, reduce wear, reduce noise and vibration, so the friction of the work is more stable and longer service life.
【技术实现步骤摘要】
一种铁基粉末冶金摩擦材料
本专利技术涉及摩擦材料
，具体涉及一种铁基粉末冶金摩擦材料。
技术介绍
粉末冶金摩擦材料是以金属及其合金为基体,添加摩擦组元和润滑组元,用粉末冶金技术制成,主要用于制造摩擦式制动器与摩擦式离合器的摩擦片。由于该材料具有摩擦因数高且稳定、耐磨性好、磨合性好、导热性优良、环境污染小、强度高、使用负荷高及工作平稳可靠等优点，由于粉末冶金的种种优点，粉末冶金相关企业已经适用于汽车行业、装备制造业、金属行业、航空航天、军事工业、仪器仪表、五金工具、电子家电等领域的零配件生产和研究，相关原料、辅料生产，各类粉末制备设备、烧结设备制造。产品包括轴承、齿轮、硬质合金刀具、模具、摩擦制品等等。军工企业中，重型的武器装备如穿甲弹，鱼雷等，飞机坦克等刹车副均需采用粉末冶金技术生产。粉末冶金汽车零件近年来已成为为中国粉末冶金行业最大的市场，约50%的汽车零部件为粉末冶金零部件。粉末冶金摩擦材料按基体成分可分为铜基和铁基两大类。虽然铁基的比铜基的有稍高的硬度、强度、摩擦系数，允许承受的工作比压和表面瞬时温度也较高；但是较差的耐热系数和较高的磨损率。磨损率过大...
【技术保护点】
一种铁基粉末冶金摩擦材料，其特征在于：包括以下重量份数的原料组成：铁粉55~72份，铜粉6~15份，石墨4~10份，二氧化硅粉3~6份，碳化硼粉2~5份，碳化硅粉3~6份，二氧化钼粉2~6份，二氧化锆粉1~4份，沉淀硫酸钡粉3~10份，氧化铬粉1~3份，镍粉1~4份。
【技术特征摘要】
1.一种铁基粉末冶金摩擦材料，其特征在于：包括以下重量份数的原料组成：铁粉55~72份，铜粉6~15份，石墨4~10份，二氧化硅粉3~6份，碳化硼粉2~5份，碳化硅粉3~6份，二氧化钼粉2~6份，二氧化锆粉1~4份，沉淀硫酸钡粉3~10份，氧化铬粉1~3份，镍粉1~4份。2.根据权利要求1所述一种铁基粉末冶金摩擦材料，其特征在于：所述铁粉为200目、铜粉为250目、石墨为80目、镍粉150目。3.根据权利要求1所述一种铁基粉末冶金摩擦材料，其特征在于：所述二氧化硅粉、碳化硼粉、碳化硅粉、二氧化钼粉、二氧化锆粉、沉淀硫酸钡粉和氧化铬粉为100~200目。4.根据权利要求1所述...
【专利技术属性】
技术研发人员：张美红，
申请(专利权)人：苏州曼里尼斯金属科技有限公司，
类型：发明
国别省市：江苏,32