The invention discloses a preparation method, including: PTFE rods with PTFE powder as raw material, the hot extrusion extruder, extruder, and control the hot pressing temperature and extrusion pressure, to prepare the length of 10m and diameter of 4mm 500m 60mm a.. The use of PTFE rods for the invention discloses a preparing method of PTFE rods has good thermal stability and not easy to break the advantages, can be used as the core of hydraulic rubber hose, no deformation after repeated use in curing temperature of hydraulic rubber hose, hydraulic rubber hose production with reduced scrap cost can control the hydraulic rubber mandrel. The hose diameter size, improve the quality of hydraulic rubber hose, greatly improve the qualified rate of hydraulic rubber hose.
【技术实现步骤摘要】
一种聚四氟乙烯棒的制备方法及其应用
本专利技术涉及高分子材料
，更具体地说，本专利技术涉及一种聚四氟乙烯棒的制备方法，本专利技术还涉及一种聚四氟乙烯棒制备方法制备的聚四氟乙烯棒的应用。
技术介绍
液压橡胶软管常使用橡胶棒和PP棒作为芯棒，但是橡胶棒和PP棒使用寿命短，容易断裂，在经过多次处于130-170℃的高温时会发生软化、老化，使芯棒发生变形，而液压橡胶软管内径的控制主要是靠芯棒的尺寸来控制，芯棒的变形会造成芯棒的直径不均匀，直接影响了液压橡胶软管的内径。一般橡胶棒及PP棒使用30-50次就要报废更换，大大增加生产成本。聚四氟乙烯棒，俗称铁氟龙棒，可用于化工、机械、电子电器和医用等领域，具有加高的热稳定性，在300-500℃时也不会发生变形，但是市场上生产的铁氟龙棒只有1-5m长，而液压橡胶软管用到的芯棒的长度要在10m-200m左右，因此市场上生产的聚四氟乙烯棒并不能作为液压橡胶软管生产使用的芯棒。专利号为CN101011854A的中国专利公开了一种聚四氟乙烯棒材热压挤出的制备方法及其专用热压挤出机，其通过两个顶杆和两条挤出管的配合，提高了聚四氟乙烯棒...
【技术保护点】
一种聚四氟乙烯棒的制备方法，其特征在于，包括：以聚四氟乙烯粉料为原料，将其置于热压挤出机进行挤出，并控制热压挤出机的挤出温度和挤出压力，以制备得到长度为10m‑500m且直径为4mm‑60mm的聚四氟乙烯棒。
【技术特征摘要】
1.一种聚四氟乙烯棒的制备方法，其特征在于，包括：以聚四氟乙烯粉料为原料，将其置于热压挤出机进行挤出，并控制热压挤出机的挤出温度和挤出压力，以制备得到长度为10m-500m且直径为4mm-60mm的聚四氟乙烯棒。2.根据权利要求1所述的一种聚四氟乙烯棒的制备方法，其特征在于，热压挤出机的挤出温度为330-400℃，挤出压力为15-35Mpa。3.根据权利要求2所述的一种聚四氟乙烯棒的制备方法，其特征在于，热压挤出机的挤出速度为0.3-0.6m/h。4.根据权利要求2所述的一种聚四氟乙烯棒的制备方法，其...
【专利技术属性】
技术研发人员：罗伯祥，罗文畅，李培光，
申请(专利权)人：广州畅业橡胶石油设备有限公司，
类型：发明
国别省市：广东,44