一种隔热抗紫外抗菌防透面料纱线的生产方法技术

一种隔热抗紫外抗菌防透面料纱线的生产方法，属于纺织技术领域，本发明专利技术将隔热抗紫外抗菌防透仿棉聚酯短纤作为功能纤维，与棉纤维、汉麻纤维进行混纺，取得具有防透视、隔热、抗菌的功能纱线。该纱线方便后续织造成面料，并能使面料具有轻薄、柔软、舒适透气、触感自然、贴肤的优越效果，同时还具有遮体和防紫外线的基本功能。

Production method of heat insulation and anti ultraviolet antibacterial anti penetration fabric yarn

A method for producing heat insulation and UV resistant antibacterial anti permeability of fabric and yarn, belonging to the technical field of the textile, the heat insulation and UV resistant antibacterial anti permeability of cotton like polyester staple fiber as functional fiber, blended with cotton fiber, hemp fiber, made with anti perspective, heat insulation, antibacterial function of yarn. The yarn is easy to follow the fabric, and the fabric has the advantages of light, soft, comfortable, breathable, natural touch, skin, and also has the basic function of covering and anti ultraviolet.

【技术实现步骤摘要】
一种隔热抗紫外抗菌防透面料纱线的生产方法
本专利技术属于纺织
，特别涉及隔热抗紫外线抗菌防透视面料纱线的制备方法。
技术介绍
近年来，随着服装面料产品的不断升级和市场消费者的要求越来越高，多功能复合面料品种日益提高，尤其是夏季面料，要求轻薄、柔软、舒适透气、触感自然、贴肤。面料越轻薄，透气、透光性越好，但是面料的“遮体”功能就会降低，影响面料的实际服用，如果裤子、衬衣比较透的话会导致里面的内衣、内裤有所暴露，在一些场合引起尴尬。同时，颜色较浅、较薄的面料其抗热、隔绝紫外线的效果也会下降。另外，较薄、透气的面料在日常使用过程中不能有效阻挡外界热量以及紫外线，而现在由于紫外线引起的皮肤问题越来越受到消费者的重视。现有技术主要是通过以下方式来克服以上矛盾：1、采用改变纤维截面形状的方法。通过制备异形截面纤维，对光线形成折射和反射，但这种纤维对纯纺面料有效果，多混纺纱线，由于引入其他不具有此类结构的纤维，会大大削弱异性截面纤维反射光线的能力。2、采用涂层后整理加助剂的方法，在面料表面涂覆二氧化钛以实现面料的防透。但这种方法会使面料手感变差，且难以实际生产，面料表面覆盖的二氧化钛在后期服本文档来自技高网...

【技术保护点】
一种隔热抗紫外抗菌防透面料纱线的生产方法，其特征在于：将隔热抗紫外抗菌防透仿棉聚酯短纤与棉纤维、汉麻纤维进行混合，经开清棉、梳棉、并条、粗纱和细纱，得隔热抗紫外抗菌防透面料纱线。

【技术特征摘要】
1.一种隔热抗紫外抗菌防透面料纱线的生产方法，其特征在于：将隔热抗紫外抗菌防透仿棉聚酯短纤与棉纤维、汉麻纤维进行混合，经开清棉、梳棉、并条、粗纱和细纱，得隔热抗紫外抗菌防透面料纱线。2.根据权利要求1所述的生产方法，其特征在于：所述隔热抗紫外抗菌防透仿棉聚酯短纤与棉纤维、汉麻纤维的混合质量比为15～50∶15～35∶30～60。3.根据权利要求1或2所述的生产方法，其特征在于：所述隔热抗紫外抗菌防透仿棉聚酯短纤的生产方法包括将纳米二氧化钛、金属锌氧化物、陶瓷粉体和高聚物纺丝液混合后进行喷...

【专利技术属性】
技术研发人员：顾义师，唐志钢，
申请(专利权)人：江苏占姆士纺织有限公司，
类型：发明
国别省市：江苏,32