The invention discloses a high hardness wear-resistant flux cored wire, and comprises a medicine core which is wrapped in low carbon cored cold rolling steel strip outer skin, drug core raw materials according to the weight: low carbon ferrochrome 20 25 copies, 3 copies of the 1.5 titanium powder, nickel powder, calcium 2 1 5 Alloy 8 copies, 4 copies, 2 gold Mei Lvhe 3 electrolytic manganese 5 copies, 2 copies, 1 molybdenum niobium iron 2.5 4 copies, 2 copies, 1 V-Fe rare earth iron alloy 3 5 copies, 5 copies, 3 carbonate graphite 3 4 copies, 150 copies of 120 iron powder 0.5, tungsten powder 1.5, 2 4 calcium fluoride. A kind of high hardness wear-resistant cored wire provided by the invention has good welding performance, weld metal microstructure, no pores and cracks, good and stable performance with the parent material combination, and the deposited metal has good wear resistance, corrosion resistance and high hardness.
【技术实现步骤摘要】
一种耐磨高硬度药芯焊丝
本专利技术涉及焊丝
，尤其涉及一种耐磨高硬度药芯焊丝。
技术介绍
药芯焊丝作为一种常见的金属焊接材料，被广泛应用于航空航天、汽车制造、建筑、桥梁、石油化工等领域。焊接质量的好坏、焊接效率的高低是由焊接材料、焊接工艺决定的，尤其是焊接材料是焊接的关键，目前药芯焊丝还存在成分配置不合理，导致熔敷金属出现小气孔和裂纹，同时在耐磨、耐腐蚀和硬度上还有待提高。
技术实现思路
基于
技术介绍
存在的技术问题，本专利技术提出了一种耐磨高硬度药芯焊丝，其具有良好焊接性能，熔敷金属组织致密，无气孔和裂纹出现，与母材结合良好且性能稳定，且熔敷金属具有良好的耐磨、耐腐蚀和高硬度等性能。本专利技术提出的一种耐磨高硬度药芯焊丝，由药芯和包覆在药芯外侧的低碳冷扎钢带外皮组成，药芯的原料按重量份数包括：低碳铬铁20-25份、钛粉1.5-3份、镍粉1-2份、硅钙合金5-8份、镁铝合金2-4份、电解锰3-5份、钼铁1-2份、铌铁2.5-4份、钒铁1-2份、稀土铁合金3-5份、碳酸盐3-5份、石墨3-4份、铁粉120-150份、钨粉0.5-1.5份、氟化钙2-4份。具体实施例中...
【技术保护点】
一种耐磨高硬度药芯焊丝，其特征在于，由药芯和包覆在药芯外侧的低碳冷扎钢带外皮组成，药芯的原料按重量份数包括：低碳铬铁20‑25份、钛粉1.5‑3份、镍粉1‑2份、硅钙合金5‑8份、镁铝合金2‑4份、电解锰3‑5份、钼铁1‑2份、铌铁2.5‑4份、钒铁1‑2份、稀土铁合金3‑5份、碳酸盐3‑5份、石墨3‑4份、铁粉120‑150份、钨粉0.5‑1.5份、氟化钙2‑4份。
【技术特征摘要】
1.一种耐磨高硬度药芯焊丝，其特征在于，由药芯和包覆在药芯外侧的低碳冷扎钢带外皮组成，药芯的原料按重量份数包括：低碳铬铁20-25份、钛粉1.5-3份、镍粉1-2份、硅钙合金5-8份、镁铝合金2-4份、电解锰3-5份、钼铁1-2份、铌铁2.5-4份、钒铁1-2份、稀土铁合金3-5份、碳酸盐3-5份、石墨3-4份、铁粉120-150份、钨粉0.5-1.5份、氟化钙2-4份。2.根据权利要求1所述耐磨高硬度药芯焊丝，其特征在于，所述碳酸盐为碳酸钙、碳酸钡、碳酸锌、碳酸钠中...
【专利技术属性】
技术研发人员：卢齐元，
申请(专利权)人：天长市通联焊业有限公司，
类型：发明
国别省市：安徽,34