The invention discloses a antiskinning castable, belongs to the field of refractory materials, the invention is configured in accordance with the following weight percentage: particle size of silicon carbide 40~55% 1~3mm, particle size 1~5mm mullite 5~10% size 0~2.5 m calcining alpha alumina particle size is 0~0.15 1~5%, m 1~5% particle size of silicon powder, white corundum 5~10% 1~4mm powder, calcium aluminate cement 5~10%, particle size of fly ash ceramsite 3~8% 0.01~0.1mm, 5~10% 0.5~1.5mm of the particle size of aluminum sulfate, explosion-proof fiber 0.1~0.5% composite water reducing agent 0.2~0.3%. The invention can greatly reduce the generation times of the crust, and meanwhile, it is convenient to clean the crust, and has excellent characteristics of abrasion resistance, alkali resistance and earthquake resistance.
【技术实现步骤摘要】
一种抗结皮浇注料及其制备方法
本专利技术涉及耐火材料领域，具体涉及一种抗结皮浇注料及其制备方法。
技术介绍
水泥是最大宗的工业产品之一，水泥工业是我国国民经济的支柱产业。随着我国经济的发展，水泥产业的规模不断扩大，特别进入21世纪，随着新型干法水泥生产工艺和技术的成熟，我国大规格回转窑的新型干法水泥生产线数量得到了迅猛发展，这得益于新型干法水泥回转窑直径∮4.5~6m，窑长70~84m，具有窑温高、窑速快、产量大，经济效益好的优势，但也带来了窑内衬受碱侵蚀加重、结构更复杂等问题。水泥工业是典型的高能耗、高排放行业。水泥生产的主要工艺过程是首先由各种原料经破碎、粉磨后制成生料，然后再把生料送到高温窑炉中进行煅烧、形成熟料，最后将熟料与少量石膏磨细制成水泥。在生产过程中，水泥窑的内壁上会出现结皮，特别是在预热器的下斜坡、上升烟道以及锥体处，结皮通常是碱、氯等有害成分在预热器系统中循环富集产生的，害成分的最低共熔点往往很低，有的还不超过700℃，因此随着有害成分含量的增加，会使体系或体系的局部最低共熔温度下降，在预热器系统内出现液相。液相凝聚时，会以熔融态形式沉降下来，...
【技术保护点】
一种抗结皮浇注料，其特征在于，所述抗结皮浇注料的原料按照下列质量百分比进行配置：粒度为1~3mm的碳化硅 40~55%粒度为1~5mm的莫来石 5~10%粒度为0~2.5μm煅烧α氧化铝 1~5%粒度为0~0.15μm硅微粉 1~5%粒度为1~4mm的白刚玉粉 5~10%铝酸钙水泥 5~10%粒度为0.01~0.1mm的粉煤灰陶粒 ...
【技术特征摘要】
1.一种抗结皮浇注料，其特征在于，所述抗结皮浇注料的原料按照下列质量百分比进行配置：粒度为1~3mm的碳化硅40~55%粒度为1~5mm的莫来石5~10%粒度为0~2.5μm煅烧α氧化铝1~5%粒度为0~0.15μm硅微粉1~5%粒度为1~4mm的白刚玉粉5~10%铝酸钙水泥5~10%粒度为0.01~0.1mm的粉煤灰陶粒3~8%粒度为0.5~1.5mm的硫酸铝粉5~10%防爆纤维0.1~0.5%复合减水剂0.2~0.3%上述各项组分含量之和为100%。2.根据权利要求1所述抗结皮浇注料，其特征在于，所述复合减水剂为六偏磷酸钠与FDN高效减水剂以及三...
【专利技术属性】
技术研发人员：翁卫民，方秀土，
申请(专利权)人：长兴盛隆耐火材料有限公司，
类型：发明
国别省市：浙江,33