The invention discloses a grinding liquid petroleum instrument, the polishing liquid is composed of corundum particles, ice particles, ammonia, acetone, metal corrosion inhibitor and water, the volume ratio of 2: 2.5% corundum grains, grains of ice 3 5%, 5 6% ammonia, acetone was 1 1.5%. The corrosion inhibitor 4 8%, the rest is water. The invention has the advantages of adding ice particles in the slurry, so that in the grinding process, when corundum particles in contact with the workpiece grinding heat, ice is melting rapidly, since the melt will absorb a large amount of heat, and the melting of water will increase the fluidity of the grinding fluid. So, the polishing liquid heating is diluted, liquidity increases, will produce heat quickly away, achieve better cooling effect.
【技术实现步骤摘要】
一种石油仪器用研磨液
本专利技术涉及研磨领域,特别设计一种石油仪器用研磨液。
技术介绍
在研磨液研磨过程中,由于摩擦作用的存在,往往会产生大量的热量,热量的存在会导致被研磨的工件温度升高,从而影响其表面质量,更有甚者,在研磨过程中磨粒与工件接触时有可能会产生瞬间过热,导致工件局部表面晶相组织变化,影响工件便面组织的一致性,从而有可能导致工件不符合工艺要求,二现有技术中的研磨液在研磨过程中大都散热较差,因此会导致工件在研磨过程中过热(甚至局部过热),影响工件的表面性能。
技术实现思路
本专利技术要解决的技术问题是提供一种能够散热降温且防腐蚀的研磨液。为解决上述技术问题,本专利技术的技术方案为:一种石油仪器用研磨液,其创新点在于:所述研磨液由刚玉颗粒、冰粒、氨水、丙酮、金属防蚀剂以及水组成,其体积比为:刚玉颗粒2.0-2.5%,冰粒3-5%,氨水为5-6%,丙酮为1-1.5%,金属防蚀剂4-8%,其余为水。进一步的,所述刚玉颗粒2%,冰粒4%,氨水为6%,丙酮为1%,金属防蚀剂6%,其余为水。本专利技术的优点在于:在研磨液中加入冰粒,从而使得在研磨的过程中,当刚玉颗粒与工件接触研磨产生热量是,冰粒受热会迅速融化,以来其融化会吸收大量的热量,而来其融化为水后会加大研磨液的流动性,使得发热处的研磨液被稀释,流动性增大,将产生的热量迅速带离,达到较好的散热降温作用。具体实施方式下面的实施例可以使本专业的技术人员更全面地理解本专利技术,但并不因此将本专利技术限制在所述的实施例范围之中。实施例1:一种石油仪器用研磨液,研磨液由刚玉颗粒、冰粒、氨水、丙酮、金属防蚀剂以及水组成 ...
【技术保护点】
一种石油仪器用研磨液,其特征在于:所述研磨液由刚玉颗粒、冰粒、氨水、丙酮、金属防蚀剂以及水组成,其体积比为:刚玉颗粒2.0‑2.5%,冰粒3‑5%,氨水为5‑6%,丙酮为1‑1.5%,金属防蚀剂4‑8%,其余为水。
【技术特征摘要】
1.一种石油仪器用研磨液,其特征在于:所述研磨液由刚玉颗粒、冰粒、氨水、丙酮、金属防蚀剂以及水组成,其体积比为:刚玉颗粒2.0-2.5%,冰粒3-5%,氨水为5-6%,丙酮为1...
【专利技术属性】
技术研发人员:唐生荣,
申请(专利权)人:南通华兴石油仪器有限公司,
类型:发明
国别省市:江苏,32