本发明专利技术公开了一种PET塑料专用醇溶高遮盖易刮银油墨，是由下述质量分数的成分制备而成的：铝基银浆20~30%、丙烯酸树脂液25~35%、氯醋树脂液5~10%、高岭土10~15%、乙酯10~15%和异丙醇1~3%。本发明专利技术采用丙烯酸树脂液和氯醋树脂液作为连结料，制成的银油墨适用于在PET塑料上进行高速印刷，具有高度的遮盖力和适宜的附着性，既不会自动脱落，又有一定的附着性，但又不会附着的太好，且无苯无酮、安全无毒。

PET plastic special, alcohol soluble high cover, easy to scratch silver ink

The invention discloses a PET plastic special alcohol soluble high covering easy silver ink, is a component for the mass fraction prepared: aluminum silver paste and 20~30% acrylic resin liquid 25~35%, liquid chlorine vinegar resin 5~10%, 10~15%, 10~15% and kaolin ethyl isopropanol 1~3%. The invention adopts acrylic resin liquid and liquid chlorine vinegar resin as a bonding material made of silver ink suitable for high-speed printing in PET plastic, has high hiding power and suitable adhesion, does not automatically fall off, and attached some, but not too good and no attachment, no benzene ketone, safe and non-toxic.

【技术实现步骤摘要】
PET塑料专用醇溶高遮盖易刮银油墨
本专利技术涉及油墨
，特别是涉及一种PET塑料专用醇溶高遮盖易刮银油墨。
技术介绍
聚对苯二甲酸乙二醇酯，化学式为COC6H4COOCH2CH2O，（英文：Polyethyleneterephthalate，简称PET），由对苯二甲酸二甲酯与乙二醇酯交换或以对苯二甲酸与乙二醇酯化先合成对苯二甲酸双羟乙酯，然后再进行缩聚反应制得。铝基银浆，为铝粉通过特殊的表面处理工艺与相应溶剂制成的颜料，能够对可见光反射呈银白色，使其具有良好的装饰性能和遮盖性能。但是现有技术的易刮银油墨，性能一般都不够稳定，刮除不够方便彻底，亦或是生产过程复杂，生产过程及原料不够环保。
技术实现思路
本专利技术主要解决的技术问题是提供一种PET塑料专用醇溶高遮盖易刮银油墨，适用于PET基材。为解决上述技术问题，本专利技术采用的一个技术方案是：提供一种PET塑料专用醇溶高遮盖易刮银油墨，是由下述质量分数的成分制备而成的：铝基银浆20~30%、丙烯酸树脂液25~35%、氯醋树脂液5~10%、高岭土10~15%、乙酯20~25%和异丙醇1~3%。在本专利技术一个较佳实施例中，所述铝基银本文档来自技高网...

【技术保护点】
一种PET塑料专用醇溶高遮盖易刮银油墨，其特征在于，是由下述质量分数的成分制备而成的：铝基银浆20~30%、丙烯酸树脂液25~35%、氯醋树脂液5~10%、高岭土10~15%、乙酯20~25%和异丙醇1~3%。

【技术特征摘要】
1.一种PET塑料专用醇溶高遮盖易刮银油墨，其特征在于，是由下述质量分数的成分制备而成的：铝基银浆20~30%、丙烯酸树脂液25~35%、氯醋树脂液5~10%、高岭土10~15%、乙酯20~25%和异丙醇1~3%。2.根据权利要求1所述的PET塑料专用醇溶高遮盖易刮银油墨，其特征在于，所述铝基银浆为3305银浆，所述铝基银浆的粒径为6微米。3.根据权利要求1所述的PET塑料专用醇溶高遮盖易刮银油墨，其特征在于，所述丙烯酸树脂液A-14丙烯酸树脂溶解在醋酸乙酯与异丙醇的混合液中，所述醋酸乙酯与所述异丙醇的质量比为1:1。4.根据权利要求1或3所述的PET塑料专用醇溶高遮盖易刮银油墨，其特征在于，所述丙烯酸树脂液的固含量为20%。5.根据权利要求4所述的PET塑料专用醇溶高遮...