The invention provides an aluminate coupling agent formula and a preparation method thereof. The formula comprises the following components: paraffin wax, stearic acid, white oil and aluminum isopropoxide, the mass percentage is 13-18:35-45:30-40:8-12. The preparation method includes: (1) the first the first white oil, paraffin and stearic acid at a temperature of 70-100 reaction, which was the first mixture; (2) second and second paraffin oil, aluminum isopropoxide reaction in the temperature of 70-100 Deg. C, then adding the first mixture is cooled to obtain the coupling agent. Effect of coupling agent of the invention strength, filling the surface of inorganic Gaby; full activation of more than 98%; the surface strong chemical bond, completely blending with organic matter.
【技术实现步骤摘要】
本专利技术涉及偶联剂及其制备
，特别是指一种铝酸酯偶联剂的配方及其制备方法。
技术介绍
经铝酸酯偶联剂活化改性处理的各种无机粉体，因其表面发生化学或物理化学作用生成一有机分子层，由亲水性变成亲有机性。实践证明，无机粉体表面经铝酸酯偶联剂改性后用于复合制品中，偶联剂的亲无机端与亲有机端能分别与无机填料表面和有机树脂发生化学反应或形成缠结结构，增强了无机粉体与有机树脂的界面相容性，所以用铝酸酯偶联剂改性，不仅可以改善填充无机粉体的塑料制品的加工性能，而且也可以明显改善制品的物理机械性能，使产品吸水率降低，吸油量减少，填料分散匀均。对于一些低填充的塑料制品，一般可大幅度增加填料用量(比原填充量增加一倍或一倍以上)，改善加工性能(熔体粘度下降，对模具磨损减少)，提高产品质量，降低生产成本，因而具有明显的经济效益。但是现有铝酸酯偶联剂具有强度较小、相容性差差的缺点，因此研发一种作用强度大，相容性好的偶联剂还是很有必要的。
技术实现思路
...
【技术保护点】
一种铝酸酯偶联剂的配方，包括如下组分：石蜡、硬脂酸、白油和异丙醇铝，其质量百分比为：13‑18:35‑45:30‑40:8‑12。
【技术特征摘要】
1.一种铝酸酯偶联剂的配方，包括如下组分：石蜡、硬脂酸、白油和异丙
醇铝，其质量百分比为：13-18:35-45:30-40:8-12。
2.根据权利要求1所述的一种铝酸酯偶联剂的配方，其特征在于，所述配
方中石蜡、硬脂酸、白油和异丙醇铝的质量百分比为15:35-45:30-40:8-12。
3.根据权利要求1或2所述的一种铝酸酯偶联剂的制备方法，包括：
(1)将第一白油、第一石蜡和硬脂酸在温度为70-100℃反应，即得第一混合
物；
(2)将第二白油、异丙醇铝和第二石蜡在温度至70-100℃反...