The invention discloses an antistatic adhesive, this adhesive according to the weight percentage consists of the following components: vinyl acetate methyl methacrylate:: 40%; 10%; 5%; 1-3%: PVA: dibutyl phthalate; shell carbon black: 1-5%; the rest is water. The preparation method comprises the following steps: in an electric mixer, constant pressure funnel, a condenser, a thermometer four mouth bottle, add water and alcohol, heating to 65 Deg. C, adding a free radical initiator, and then heated to 75 DEG C, adding vinyl acetate and methyl methacrylate, keep the temperature for 5 hours; cooling. The shell carbon black and dibutyl phthalate added slowly stir, namely the product. As a result of adding a proper amount of shell carbon black, the adhesive has good antistatic properties. On the basis of ensuring that the adhesive has a large enough shear strength, the adhesive has good stability during storage.
【技术实现步骤摘要】
本专利技术属于胶粘剂领域，具体涉及抗静电无醛胶粘剂及其制备方法。
技术介绍
随着电子技术的广泛应用，促进了科技的发展与经济的繁荣。但同时也造成了静电积聚和静电放电现象的频繁发生，给工业生产和生态环境带来众多危害。所以抗静电无醛胶粘剂作为静电场所的粘接材料日益受到人们的重视。现用的抗静电胶粘剂都是在通用粘合剂中掺入金属粉等得到。但金属粉和胶粘剂聚合物树脂的相克性差，使得粘合剂的储存稳定性差。
技术实现思路
本专利技术所要解决的技术问题是：针对现有技术存在的不足，提供一种抗静电效果佳，储存稳定性好的抗静电无醛胶粘剂及其制备方法。为实现本专利技术之目的，采用以下技术方案予以实现：一种抗静电无醛胶粘剂，该胶粘剂按重量百分比计由以下组分构成：醋酸乙烯40%；甲基丙烯酸甲酯：10%；聚乙烯醇：5%；邻苯二甲酸二丁酯：1-3%；谢尔炭黑：1-5%；其余为水。作为优选方案：所述的谢尔炭黑含量为2%。本专利技术还提供一种上述胶粘剂的制备方法，包括以下步骤：在装有电动搅拌器、...
【技术保护点】
一种抗静电无醛胶粘剂，其特征在于：该胶粘剂按重量百分比计由以下组分构成：醋酸乙烯40%；甲基丙烯酸甲酯：10%；聚乙烯醇：5%；邻苯二甲酸二丁酯：1‑3%；谢尔炭黑：1‑5%；其余为水。
【技术特征摘要】
1.一种抗静电无醛胶粘剂，其特征在于：该胶粘剂按重量百分比计由以下组分构成：
醋酸乙烯40%；
甲基丙烯酸甲酯：10%；
聚乙烯醇：5%；
邻苯二甲酸二丁酯：1-3%；
谢尔炭黑：1-5%；
其余为水。
2.根据权利要求1所述的一种抗静电无醛胶粘剂，其特征在于：所述的谢尔炭黑含量为2...