The present invention provides a method for preparing waterborne heat sealing glue, the surface active agent, plasticizer, triethanolamine and polyol added to the water, and then the obtained mixture is dispersed, heating, adding acrylic acid, chloroprene rubber, polyvinyl alcohol, thermal insulation, and then the mixture is added to polyvinyl acetate resin the emulsion, pH adjusted to 6 8, finally adding thickening agent, stirring, can. The invention adopts the emulsion plasticizer modified prepared by heat sealing glue, containing polyvinyl acetate resin glue is not flexible, tortuous degumming, heat sealed never degumming.
【技术实现步骤摘要】
一种水性热封胶的制备方法
本专利技术属于包装材料
，具体涉及一种水性热封胶的制备方法。
技术介绍
热封胶是一种包装用胶，是预先涂布干燥备用的胶粘剂，具有良好的粘基力尤其适合于纸张等的粘合，用作封口时象纸—塑复合材料，经热压即完成粘接。因热合温度较低，又由于有纸张的支持，不会象塑料膜那样遇到过热而产生变形。与冷封胶相比，其不同点是：(1)冷封胶使用的是涂布面对涂布面冷压对粘完成粘接的，而热封胶是涂布面对非涂布面(如包装纸)热压粘接的，即热封胶的两个工作面中只需一个面预涂胶，因而可以减少涂布的工作量。(2)热封胶经干燥后涂布面的粘性比冷封胶更低，不存在压敏性。收卷存放时不会对纸等背材形成牢固的粘合，所以解卷将更容易。(3)冷封胶是直接涂布在包装材料上，应用时在包装机上冷压可迅速完成粘合包装和密封过程。热封胶一般是涂布在包装纸上，应用时在专用包装机上可进行热压粘合包装和密封过程，能封合塑料膜的包装封口机几乎均可用于热封胶的封口。(4)热封胶需经热压封合，一旦撕开即被破坏，所以防盗保密功能较好。(5)冷、热封胶的涂布量都很低，冷封胶一般在两个工作面各涂5g/m2左右...
【技术保护点】
一种水性热封胶的制备方法，其特征在于：包括以下步骤：步骤1，以重量份计，将表面活性剂0.8‑2份、增塑剂2‑6份、三乙醇胺0.1‑0.4份、多元醇0.5‑0.9份加至水中，分散，得混合物A；步骤2，以重量份计，将混合物A升温至50‑70℃，加入丙烯酸0.3‑0.9份、氯丁橡胶0.1‑0.3份、聚乙烯醇0.2‑0.6份，保温1‑3h，得到混合物B；步骤3，以重量份计，将混合物B加至聚醋酸乙烯酯树脂乳液30‑50份中，调节pH至6.0‑8.0，得到混合物C；步骤4，以重量份计，在混合物C中加入增稠剂2‑10份，搅拌，即可。
【技术特征摘要】
1.一种水性热封胶的制备方法，其特征在于：包括以下步骤：步骤1，以重量份计，将表面活性剂0.8-2份、增塑剂2-6份、三乙醇胺0.1-0.4份、多元醇0.5-0.9份加至水中，分散，得混合物A；步骤2，以重量份计，将混合物A升温至50-70℃，加入丙烯酸0.3-0.9份、氯丁橡胶0.1-0.3份、聚乙烯醇0.2-0.6份，保温1-3h，得到混合物B；步骤3，以重量份计，将混合物B加至聚醋酸乙烯酯树脂乳液30-50份中，调节pH至6.0-8.0，得到混合物C；步骤4，以重量份计，在混合物C中加入增稠剂2-10份，搅拌，即可。2.根据...
【专利技术属性】
技术研发人员：冯文田，冯超，
申请(专利权)人：句容市兴武包装有限公司，
类型：发明
国别省市：江苏,32
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。