本发明专利技术所述的对于极小工件在回转式炉中气体渗氮的新方法，涉及一种极小型工件的气体渗氮工艺及设备。方法为：a、将工件装于回转式炉内并固定，使炉体旋转；b、对炉体进行加热，加热温度为580度，保温时间为30分钟至3小时；c、当温度达到580度时通入氨气或能够产生氮气的其他气体，通入氨气的流量一路内溢出的废气能够点燃即可。本发明专利技术具有结构新颖、简单、工艺先进、渗氮均匀、提高生产率等特点，故属于一种集经济性与实用性为一体的新型对于极小工件在回转式炉中气体渗氮的新方法。

A new method for gas nitriding in rotary kiln with minimum workpiece

The present invention relates to a new method for gas nitriding in a rotary furnace for a minimal workpiece, relating to a gas nitriding process and apparatus for extremely small workpieces. Methods: A, the workpiece is installed and fixed on the rotary furnace, the furnace body rotation; B, the furnace heating, the heating temperature is 580 degrees, the holding time is 30 minutes to 3 hours; C, when the temperature reaches 580 degrees when other gases NH3 or can produce nitrogen gas, exhaust gas flow a way to pass into the overflow of ammonia gas can be ignited. The invention has the advantages of novel structure, simple and advanced technology, improve productivity, uniform nitriding characteristics, a new method which belongs to a new set of economic and practical for small workpiece in rotary furnace gas nitriding.

【技术实现步骤摘要】

本专利技术所述的对于极小工件在回转式炉中气体渗氮的新方法，涉及一种极小型工件的气体渗氮工艺及设备。
技术介绍
传统的气体氮化是在井式炉或多用炉中进行。对于大、中型零件能保证产品质量和生产率。但对于极小零件，外径在10mm以内，厚度在2mm以内的工件就需要工装夹具来协助完成渗氮工艺，但这样的做法使得工艺夹具的用量极大，并且还不能保证极小工件渗氮层均匀一致，导致生产率大大降低。针对上述现有技术中所存在的问题，研究设计一种新型的对于极小工件在回转式炉中气体渗氮的新方法，从而克服现有技术中所存在的问题是十分必要的。
技术实现思路
鉴于上述现有技术中所存在的问题，本专利技术的目的是研究设计一种新型的对于极小工件在回转式炉中气体渗氮的新方法。用以解决现有技术中存在的：1、工艺夹具用量极大；2、不能保证极小工件渗氮均匀；3、生产率降低等问题。本专利技术的技术解决方案是这样实现的：本专利技术所述的对于极小工件在回转式炉中气体渗氮的新方法；其方法为：a、将工件装于回转式本文档来自技高网...

【技术保护点】
一种对于极小工件在回转式炉中气体渗氮的新方法；其方法为：a、将工件装于回转式炉内并固定，使炉体旋转；b、对炉体进行加热，加热温度为520‑580度；c、当温度达到520‑580度时通入氨气或能够产生氮气的其他气体，通入氨气的流量一路内溢出的废气能够点燃即可。

【技术特征摘要】
1.一种对于极小工件在回转式炉中气体渗氮的新方法；其方法为：
a、将工件装于回转式炉内并固定，使炉体旋转；
b、对炉体进行加热，加热温度为520-580度；
c、当温度达到520-580度时通入氨气或能够产生氮...