Method for preparing water-based magnetorheological fluid

The invention discloses a water-based magnetorheological fluid, belonging to the technical field of intelligent materials. Through the collection of hydrolyzed protein hydrolysis silk degumming solution, followed by melamine, urea and triethanolamine on surface grafting modified by amino groups, carbon disulfide, preparation of two dithiocarbamate protein chelating agent, and carbonyl iron sequestering on the surface of iron powder effective package, carbonyl iron powder preparation of hydrophilic protein coated, dispersing effective in water, and the water to prevent the expansion of long chain, MRF hard settlement to improve the stability of water-based magnetorheological fluid suspension system and dispersion performance and have wide application prospect.

【技术实现步骤摘要】
一种水基磁流变液的制备方法
本专利技术公开了一种水基磁流变液，属于智能材料

技术介绍
磁流变液一般是由载液、微米或亚微米尺寸的铁磁性颗粒、稳定剂等组成的悬浮体系。磁流变液的特点是:在无外加磁场时，磁流变液呈牛顿流体状态，流动性与载液基本相同。当施加一外磁场后，体系粘度瞬间增大，从自由流动状态变为半固态或固体状态，体系的屈服强度和表观粘度增加2～3个数量级。同时体系的热力学、磁、光、声等性质也会发生大幅度的改变。其中体系的屈服强度和表观粘度能够受外加磁场的调控，随着外加磁场强度的变化而变化。磁流变液的这种粘度随外加磁场发生变化的效应被称为磁流变效应。磁流变液的另一个特点是：当撤除磁场后，颗粒又能迅速地恢复到自由状态，整个材料的粘度也相应降低，重新呈牛顿流体状态，这种完全可逆的变化能在毫秒级的时间内完成。磁流变液的这一可控特性使其可以在许多领域得到广泛应用，如机械、电子、航空航天、化工、能源、冶金、仪表、环保、医疗等。现阶段磁流变液的研究还是主要关注在油基磁流变液上，而关于制备水基磁流变液的报道较少。近几年，随着磁流变抛光技术的发展，水基磁流变液的研究与开发越来越受到重视。与其本文档来自技高网...

【技术保护点】
一种水基磁流变液，其特征在于：由以下重量份组成：45～50份改性蛋白螯合剂溶液、5～10份正硅酸乙酯、3～5份200目羰基铁粉和13～15份去离子水。

【技术特征摘要】
1.一种水基磁流变液，其特征在于：由以下重量份组成：45～50份改性蛋白螯合剂溶液、5～10份正硅酸乙酯、3～5份200目羰基铁粉和13～15份去离子水。2.根据权利要求1所述的一种水基磁流变液，其特征在于：所述的羰基铁粉粒径为200目。3.根据权利要求1所述的一种水基磁流变液，其特征在于：所述的改性蛋白螯合剂溶液制备步骤为，按重量份数计，由45～50份去离子水、10～15份三聚氰胺、5～8份甲醇、5～10份尿素、3～5份三乙醇胺和9～10份蚕丝蛋白浓缩液搅拌混合，经调节pH至8.0后，得碱化蛋白液，按体积比1:12，将二...