一种低温脱脂剂及其生产方法技术

本发明专利技术属于金属表面处理技术领域，具体为一种低温脱脂剂及其生产方法。本发明专利技术的低温脱脂剂，按总质量为100份计，具体组分和组成如下：脂肪醇聚氧乙烯醚硫酸钠5～7份、脂肪醇聚氧乙烯醚5～7份、椰油酸二乙醇酰胺2～4份、三乙醇胺7～9份、尿素3～5份、助溶剂6～8份、其余余量为水；本发明专利技术的脱脂剂在冬季可以实现常温脱脂，同时脱脂时间短、净洗程度高、不含磷物质、生物降解性能好、泡沫低。

Low temperature degreasing agent and production method thereof

The invention belongs to the technical field of metal surface treatment, in particular to a low temperature degreasing agent and a production method thereof. Low temperature degreasing agent of the invention, according to the total mass of 100 copies, the specific composition is as follows: fatty alcohol polyoxyethylene ether sodium sulfate is 5 ~ 7, 5 ~ 7 fatty alcohol polyoxyethylene ether, coconut oil acid two ethanol amide 2 - 4, 7 - 9, urea triethanolamine 3 - 5, 6 solvent - 8, the rest of the balance of water; degreasing agent of the invention can be realized at room temperature in winter and short time, degreasing, degreasing cleaning degree is high, no phosphorus material, biodegradability, low foam.

【技术实现步骤摘要】
一种低温脱脂剂及其生产方法
本专利技术涉及一种低温脱脂剂及其生产方法，属于金属表面处理

技术介绍
金属制品堪称全球最广泛的用品之一，也因此，金属制品的清洗是重要的研究方向。高温碱液除油是目前金属表面加工行业使用的流行的金属表面脱脂的方法，它具有脱脂效果好、除油速度快的优点。但其缺点是使用过程中需要加温，这增加了能源的消耗。伴随着国际资源的日趋紧张和国内外环保意识的增强，常温环保无污染的油污清洗剂的研发越来越受到关注。目前，常温除油是工业上金属表面脱脂的一种技术趋势。中国专利申请(申请号：201310151411.6)“一种常温脱脂剂及其制备方法”中公开了一种常温脱脂配方，它以表面活性剂和磷酸盐及强碱作为脱脂的主要组分，可以实现常温脱脂的结果，但是却具有脱脂时间长(5度下30分钟)、对环境污染(含有磷酸盐)、不能与酸兼容(含有氢氧化钠)实现脱脂除锈二合一等缺点。这对金属表面的处理来讲，需要更多的工序来完成金属表面涂装之前的前处理，也限制了配方的进一步应用。中国专利申请(申请号：201310688604.7)公开了一种常温中性脱脂剂及其生产方法。根据实施结果发现，该配方对金属表本文档来自技高网...

【技术保护点】
一种低温脱脂剂，其特征在于，按照总质量为100份计，其组分和组成如下：

【技术特征摘要】
1.一种低温脱脂剂，其特征在于，按照总质量为100份计，其组分和组成如下：2.根据权利要求1所述的低温脱脂剂，其特征在于，助溶剂为含氧的低碳有机溶剂。3.根据权利要求1所述的低温脱脂剂，其特征在于，低温脱脂剂的HLB值在10～10.6之间，pH值在8～9之间。4.一种根据权利要求1所述的低温脱脂剂的生产方...

【专利技术属性】
技术研发人员：万传云，刘喜亚，
申请(专利权)人：上海应用技术大学，
类型：发明
国别省市：上海,31