The invention relates to an adhesive field, specifically relates to a two-component water-borne glue aging hardening resistance, including A and B components, which comprises the following components: A weight fractions: waterborne neoprene milk 39 41 copies, 40 copies, 30 acrylic emulsion water terpene of tackifying resin 7 9, twelve 2 sodium 10; B components by weight components: 5 rosin 10 copies, 5 copies, 1 isocyanate fumed silica 1 3 copies, 30 copies of 40 deionized water, glue of the present invention has anti aging excellent performance in leather, sponge, to see the adhesive strength, speed and stability has very excellent effect.
【技术实现步骤摘要】
一种耐老化抗硬化的双组分水性喷胶及其制备方法
本专利技术涉及化工领域，具体地说，涉及一种耐老化抗硬化的双组分水性喷胶及其制备方法。
技术介绍
双组份喷胶主要应用于海绵、木材、皮革、布料、泡沫等材料之间的粘合，尤其对海绵与皮革、海绵与木板的弧度粘合有较强的粘接力。现有的双组份喷胶急需解决如下问题：传统的双组份喷胶在连接固化后，胶层容易硬化，特别是连接处边缘硬化尤为严重；此外对于油性较重的皮革以及仿皮材料，传统的喷胶抗油性差，特别是初粘力和终粘力不够理想，直接影响皮革、海绵间的弧度粘合牢固性和稳定性。
技术实现思路
本专利技术的目的是提供一种耐老化抗硬化的双组分水性喷胶及其制备方法，该喷胶具有优异的抗老化性能，对于皮革、海绵见的连接强度、速度和稳定性具有非常优异的效果。本专利技术提供的技术方案为：一种耐老化抗硬化的双组分水性喷胶，包括A组分和B组分，其中：A组分包括以下重量份组分：水性氯丁橡胶乳39-41份、丙烯酸乳液30-40份、水性萜烯增粘树脂7-9份、十二烷基苯磺酸钠2-10份；B组分由以下重量份组分组成：松香树脂5-10份、异氰酸酯类1-5份、气相二氧化硅1-3份...
【技术保护点】
一种耐老化抗硬化的双组分水性喷胶，其特征在于：包括A组分和B组分，其中：A组分包括以下重量份组分：水性氯丁橡胶乳39‑41份、丙烯酸乳液30‑40份、水性萜烯增粘树脂7‑9份、十二烷基苯磺酸钠2‑10份；B组分由以下重量份组分组成：松香树脂5‑10份、异氰酸酯类1‑5份、气相二氧化硅1‑3份、去离子水30‑40份。
【技术特征摘要】
1.一种耐老化抗硬化的双组分水性喷胶，其特征在于：包括A组分和B组分，其中：A组分包括以下重量份组分：水性氯丁橡胶乳39-41份、丙烯酸乳液30-40份、水性萜烯增粘树脂7-9份、十二烷基苯磺酸钠2-10份；B组分由以下重量份组分组成：松香树脂5-10份、异氰酸酯类1-5份、气相二氧化硅1-3份、去离子水30-40份。2.根据权利要求1所述的耐老化抗硬化的双组分水性喷胶，其特征在于：所述的A组分包括以下重量份组分：水性氯丁橡胶乳40份、丙烯酸乳液35份、水性萜烯增粘树脂8份、十二烷基苯磺酸钠6份；B组分由以下重量份组分组成：松香树脂7份、异氰酸酯类3份、气相二氧化硅2份、去离子水35份。3.根据权利要求1所述的耐老化抗硬化的双组分水性喷胶，其特征在于：所述的A组分中还包括1-3重量份的水玻璃。4.根据权利要求3所述的耐老化抗硬化的双组分水性喷胶，其特征在于：所述的A组分中...
【专利技术属性】
技术研发人员：李满林，
申请(专利权)人：广东泰强化工实业有限公司，
类型：发明
国别省市：广东,44
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。